Local vibrational modes in the region of the acoustic and optical phonons are reported for Mg-doped GaN grown by molecular beam epitaxy. The modes, studied by Raman spectroscopy, appear in addition to the known modes in the high-energy region around 2200 cm Ϫ1. We suggest disorder-activated scattering and scattering from Mg-related lattice vibrations to be the origin of the low-energy modes. Our assignment is supported by calculations based on a modified valence-force model of Kane. Temperature-dependent measurements between 4 and 300 K exclude an electronic Raman-scattering mechanism. We also report a new line at 2129 cm Ϫ1 and discuss the origin of all five observed high-energy modes.

No abstract

GaN layers were grown by molecular beam epitaxy and doped with carbon of nominal concentrations ranging from 1016 cm−3 to 1020 cm−3. The incorporation of carbon leads to a reduction of the background electron concentration by one order of magnitude but the material remains n-type. For high carbon concentrations a re-increase of the carrier concentration is observed which is related to selfcompensation. Investigations of the donor-acceptor-pair luminescence show that doping with carbon is accompanied by the generation of a new donor exhibiting a thermal activation energy of about 55 meV. Layers grown by atomic layer epitaxy are marked by an increased intensity of the donor-acceptor-pair band luminescence which is attributed to the enforced incorporation of carbon onto the nitrogen sublattice. The yellow luminescence is found to be a typical feature of all carbon doped layers in contrast to nominally undoped samples.

No abstract

No abstract