Crack-free AlGaN/GaN high-electron-mobility transistors (HEMTs) grown on a 200 mm Si substrate by metal–organic chemical vapor deposition (MOCVD) is presented. As grown epitaxial layers show good surface uniformity throughout the wafer. The AlGaN/GaN HEMT with the gate length of 1.5 µm exhibits a high drain current density of 856 mA/mm and a transconductance of 153 mS/mm. The 3.8-µm-thick device demonstrates a high breakdown voltage of 1.1 kV and a low specific on-resistance of 2.3 mΩ cm2 for the gate–drain spacing of 20 µm. The figure of merit of our device is calculated as 5.3×108 V2 Ω-1 cm-2.

No abstract

We report recessed-gate Al2O3/AlGaN/GaN normally-OFF metal–oxide–semiconductor high-electron-mobility transistors (MOS-HEMTs) on 8 in. Si. The MOS-HEMTs showed a maximum drain current of 300 mA/mm with a high threshold voltage of +2.4 V. The quite low subthreshold leakage current (∼10−8 mA/mm) yielded an excellent ON/OFF current ratio (9 × 108) with a small, stable subthreshold slope of 74 mV/dec. An atomic-layer-deposited Al2O3 layer effectively passivates, as no significant drain current dispersions were observed. A high OFF-state breakdown voltage of 825 V was achieved for a device with a gate-to-drain distance of 20 µm at a gate bias of 0 V.

No abstract

We have developed a large‐scale metal‐organic vapor phase epitaxy (MOVPE) reactor. The growth rates of AlN and AlGaN were compared with those calculated using the parasitic chemical reaction model. The calculated results were in good agreement with the experimental results over the entire 8″ wafer. To experimentally investigate the extent of the gas‐phase prereaction between the precursors and ammonia, the results of epitaxy were compared with those for a 6″‐type reactor. The growth of AlN and AlGaN at relatively high rates without any significant gas‐phase prereaction was demonstrated. (© 2013 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)