Hydrated products, such as (hydrated) cement pastes, decomposition through physical-chemical alterations when submitted to high temperatures. One of the main factors that lead to microstructural changes during calcination up to 800ºC, is the dehydration phases of hydrated Portland
cement. The present study sought to characterize crystalline phases occurring before and after calcination to the produced pastes using X-ray diffraction (XRD) analysis. Cement pastes were produced using Portland cement CP V-ARI RS, similar to type II (ASTM C150-07), with water/cement ratio
0.5. After a 28-day curing period, the pastes were calcinated at 800°C for 60 minutes with a 10°C/min heating rate. Afterwards, the newly produced hydraulic binder was cooled abruptly and reactivated through a rehydration process, and underwent analyses on the 7 and 28 day. During
this study it was observed that the originally hydrated products can be rehydrated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.