This study investigated the effects of different substrates on the mechanical properties of Ti-60at%Ni shape memory alloys (SMA). Two types of samples were prepared for this experiment: (1) a Ti-60at%Ni deposited on SiNx, and (2) a Ti-60at%Ni deposited on SiNx/Cr; both had a 600 nm thick film of Ti-60at%Ni. Deposition was done using the physical vapor deposition (PVD) process, and the microstructural changes and crystallization phase changes were observed through scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results showed that the TiNi thin film with a Cr adhesion layer had better mechanical properties. The bulge test showed that TiNi thin film with a Cr adhesion had a higher Young’s modulus and lower residual stress. From the thermal cycling experiment, it was found that the Cr adhesion layer buffered the mismatch between TiNi and SiNx. Additionally, the thermal cycling test was also used to measure the thermal expansion coefficient of the films, and the fatigue test showed that the Cr layer significantly improved the fatigue resistance of the TiNi film.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.