A simple method for the conception of mesoporous zeolite Y crystals with a narrow intracrystalline mesopore size distribution is reported. It involves the pseudomorphic transformation of parent zeolite crystals by recrystallisation in the presence of surfactants, and leads to two interconnected pore systems in the zeolite crystals.

No abstract

Using a simple route for preparing uniform spherical mesoporous MCM-41 materials based on a one-step synthesis in an all-water medium, we have investigated the effects of changes of the surfactant composition. The morphology, texture and structure of five samples with different compositions reveal that both, the external organization and internal pore structure, are governed by the silicate:surfactant ratio. The intake of fluids into the poressan important issue for the use of this material in biotechnology such as localized drug delivery, vectorization of drugs, biosensing applications, and biochemical separationsswas checked and confirmed.

The texture of mesoporous FAU-Y (FAUmes) prepared by surfactant-templating in basic media is a subject of debate. It is proposed that mesoporous FAU-Y consists of: (1) ordered mesoporous zeolite networks formed by a surfactant-assisted zeolite rearrangement process involving local dissolution and reconstruction of the crystalline framework, and (2) ordered mesoporous amorphous phases as Al-MCM-41, which coexist with zeolite nanodomains obtained by a dissolution-reassembly process. By the present systematic study, performed with FAU-Y (Si/Al = 15) in the presence of octadecyltrimethylammonium bromide and 0 < NaOH/Si ratio < 0.25 at 115 °C for 20 h, we demonstrate that mesoporous FAU zeolites consist, in fact, of a complex family of materials with textural features strongly impacted by the experimental conditions. Two main families have been disclosed: (1) for 0.0625 < NaOH/Si < 0.10, FAUmes are ordered mesoporous materials with zeolite walls, which coexist with zeolite nanodomains (100-200 nm) and (2) for 0.125 < NaOH/Si < 0.25, FAUmes are ordered mesoporous materials with amorphous walls as Al-MCM-41, which coexist with zeolite nanodomains (5-100 nm). The zeolite nanodomains decrease in size with the increase of NaOH/Si ratio. Increasing NaOH/Si ratio leads to an increase of mesopore volume, while the total surface area remains constant, and to a decrease of strong acidity in line with the decrease of micropore volume. The ordered mesoporous materials with zeolite walls feature the highest acidity strength. The ordered mesoporous materials with amorphous walls present additional large pores (50-200 nm), which increase in size and amount with the increase of NaOH/Si ratio. This alkaline treatment of FAU-Y represents a way to obtain ordered mesoporous materials with zeolite walls with high mesopore volume for NaOH/Si = 0.10 and a new way to synthesize mesoporous Al-MCM-41 materials containing extralarge pores (50-200 nm) ideal for optimal diffusion (NaOH/Si = 0.25).

No abstract