In humid air, copper and its high copper alloys (bronze) tend to form an oxide layer (patina). Natural patinas protect copper and its alloys from further corrosion processes. On the other hand, artists have frequently deliberately patinated bronze for visual effects. Thus, it is of great importance to study the patina changing mechanism to follow its chemical changes and to predict in advance the likely corrosion processes. Green chloride and green nitrate patinas, applied over the brown artist's patina, were tested, and also brown patina and the patina that develops on bare bronze. The Raman spectra were studied after chemical patination, and after exposing the patina samples in a climatic chamber, which can produce an environment that resembles an industrial atmosphere, for 12 weeks. The structures of the patinas and of the corrosion products were characterized by scanning electron microscopy, Raman spectroscopy and X-ray diffraction. Cuprite and cuprous sulfite were found on the brown patina, atacamite on the green chloride patina, and a mixture of gerhardite and rouaite on the blue to green nitrate type patina. After 12 weeks of exposure to humidity, a controlled concentration of SO 2 , and salt spray mist, the corrosion products changed. In general, clinoatacamite and paratacamite are the end corrosion products, after an intermediate brochantite stage on the green chloride and green nitrate type patinas. The end products of each patina type are given.

No abstract

h i g h l i g h t s Two artificial ageing processes well simulate outdoor patinas of as-cast bronze. Distribution of chemical elements are detailed according to exposure conditions.-Surface characterization with in situ FIB cross-section highlights decuprification phenomenon. Alpha (Cu) solid solution is anodic towards (alpha þ delta) eutectoid. Nano-porosities are evidenced within patinas according to corrosion process.

No abstract

No abstract