The structure and hydrogen bonding of water in the vicinity of carboxybetaine homopolymer (poly[1-carboxy-N,N-dimethyl-N-(2'-methacryloyloxyethyl)methanaminium inner salt] (PolyCMB), and a random copolymer of CMB and n-butyl methacrylate, Poly(CMB-r-BMA), with various molecular weights were analyzed in their aqueous solutions and thin film with contours of O-H stretching of Raman and attenuated total reflection infrared (ATR-IR) spectra, respectively. The relative intensity of the collective band (C value) corresponding to a long-range coupling of O-H stretchings of the Raman spectra for aqueous solution of Poly(CMB-r-BMA) was very close to that for pure water, which is in contrast with the smaller C value in aqueous solution of ordinary polyelectrolytes. The number of hydrogen bonds collapsed by the presence of one monomer residue (N(corr) value) of PolyCMB and Poly(CMB-r-BMA) (CMB, 45 mol %) (M(w), 1.14 x 10(4) and 1.78 x 10(4), respectively) could be calculated from the C value. The N(corr) values were much smaller than those for ordinary polyelectrolytes and close to those for nonionic water-soluble polymers such as poly(ethylene glycol) and poly(N-vinylpyrrolidone). Furthermore, a water-insoluble Poly(CMB-r-BMA) with a large BMA content (M(w) = 347 kD, CMB 27 mol %) could be cast as a thin film (thickness, ca. 10 microm) on a ZnSe crystal for the ATR-IR analyses. At an early stage of sorption of water into the Poly(CMB-r-BMA) film, the O-H stretching band of IR spectra for the water incorporated in the film was similar to that for free water, which is in contrast with the drastic change in the O-H stretching band of water incorporated in polymer films such as poly(methyl methacrylate) (PMMA) and poly(n-butyl methacrylate) (PBMA). The theoretical vibrational frequency for water molecules hydrating a betaine molecule calculated by using a density functional method supported the experimental results. The adhesion of human platelets to Poly(CMB-r-BMA) films was much less than that to PMMA and PBMA. With an increase in the content of CMB residue, the number of platelets adhered to the Poly(CMB-r-BMA) film drastically decreased and then gradually increased, probably due to the increase in the roughness of the film surface. These results suggest that the carboxybetaine monomer residues with a zwitterionic structure do not significantly disturb the hydrogen bonding between water molecules in both aqueous solution and thin film systems, resulting in the excellent blood-compatibility of the carboxybetaine polymers.
The structure and hydrogen bonding of water in the vicinity of a thin film of a sulfobetaine copolymer (poly[(N,N-dimethyl-N-(3-sulfopropyl)-3'-methacrylamidopropanaminium inner salt)-ran-(butyl methacrylate)], poly(SPB-r-BMA)), were analyzed with band shapes of O-H stretching of attenuated total reflection infrared (ATR-IR) spectra. The copolymer could be cast as a thin film, of approximate thickness 10 microm, on a ZnSe crystal for the ATR-IR spectroscopy. At an early stage of sorption of water into the polymer film, the O-H stretching band of the IR spectra for the water incorporated in the film was similar to that for free water. This is consistent with the tendency for another zwitterionic polymeric material, poly[(2-methacryloyloxyethylphosphorylcholine)-ran-(butyl methacrylate)] (poly(MPC-r-BMA). It is, however, contradictory to the drastic change in the O-H stretching band for water incorporated into films of polymers such as poly(2-hydroxyethyl methacrylate), poly(methyl methacrylate) and poly(butyl methacrylate). These results suggest that polymers with a zwitterionic structure do not significantly disturb the hydrogen bonding between water molecules incorporated in the thin films. The investigation into the blood-compatibility of both the poly(SPB-r-BMA) and the poly(MPC-r-BMA) films indicate a definite correlation between the blood-compatibility of the polymers and the lack of effect of the polymeric materials on the structure of the incorporated water.
The resistance of random copolymers of BMA and CMB against biofouling was evaluated. The amount of proteins adsorbed onto the CMB copolymers was smaller than that onto other polymers (non-ionic polymers and copolymers of ordinary ionic monomers and BMA) and decreased with an increase in the content of CMB residues. Furthermore, there was a dramatic decrease in the number of cells (platelets and fibroblasts) that adhered to the CMB copolymers compared with that to other polymers. In contrast with this, CMB copolymers were slightly perturbative to both complement and coagulation systems. However, the overall results suggest that zwitterionic moieties are effective for making polymer materials biocompatible due to their excellent anti-biofouling property.
The effect of a thin film of a zwitterionic random copolymer composed of carboxybetaine [1-carboxy-N,Ndimethyl-N-(2 -methacryloyloxyethyl)methanaminium inner salt] (CMB) and n-butyl methacrylate (BMA), poly(CMB-r-BMA) (CMB, 30 mol%), on the healing of a full-thickness excisional and incisional wound in hairless rats was examined. The poly(CMB-r-BMA) film significantly enhanced wound closure and complete healing of a full-thickness excisional wound compared with the effect of the poly(n-butyl methacrylate) (PBMA) and the poly(ethylene terephthalate) (PET) films. However, the poly(CMB-r-BMA) film did not enhance healing of a fullthickness incisional wound in hairless rats. The amount of proteins adsorbed and that of neutrophiles adhered onto the poly(CMB-r-BMA) film were significantly smaller than those onto the PBMA and PET films. The results suggested that various cells and growth factors in the wound exudate are utilized effectively by covering an excisional wound with the poly(CMB-r-BMA) film, resulting in acceleration of healing. In addition, the poly(CMB-r-BMA) film significantly enhanced healing of a full-thickness excisional wound in hairless rats compared with the effect of Tegaderm ® as wound dressings. The poly(CMB-r-BMA) film has potential as a new wound dressing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.