This paper presents the interaction comparison of poly(vinyl) alcohol (PVA) with hydroxyapatite derived from Spanish Mackerel (SM) and Whitefin Wolf Herring (WWH) bones, in different processing method. PVA filament and solution casting method illustrated higher crystallinity in the FTIR graph as compared to the PVA pellet and filament extrusion method. Besides, minimal interactions between PVA with glycerol and HAp was observed as well. PVA pellet and solution casting method portrait higher interaction as compared to the PVA filament and extrusion method. As for the HAp of SM and WWH, WWH had higher crystallinity and better cell adhesion with a higher Ca/P ratio while SM had relatively better mechanical strength with Ca/P ratio near to stoichiometric value. The loading of HAp (0, 2.5, 5, 10, 20, 30%) does not affect interactions of PVA/HAp composite in FTIR, and thermal properties in TGA. However, it caused an increase in crystallinity at low HAp loading and decreased at higher loading of HAp above 10%. Upon addition of HAp, tensile strength increased and elongation at break decreased. As the loading of HAp increased, both mechanical properties decreased. Scaffold with WWH composite possessed lower tensile strength and higher elongation at break than SM composite. The result of mechanical properties corresponded to the SEM result. ANOVA analysis justified the effect of HAp variations and loading on the mechanical properties of the composite was prominent.
Abstract. Nitrile gloves are widely used in the medical and automobile field due to its superiority in hypo-allergic component and chemical resistance over natural latex gloves. However, poor elastic recovery of nitrile glove to compressive force also creates an aesthetic issue for customers with high levels of wrinkling after removing from glove box. This paper demonstrates the preliminary study on the varies chemical composition such as crosslinking agents, sulphur and zinc oxide, the accelerator agent added during curing process, and the rubber filler Titanium Dioxide, on the elastic recovery and stress relaxation in nitrile gloves manufacturing. These chemical were studied at different concentration level comparing the high and low level versus the normal production range. Due to the inconsistency in the analysis technique on the surface imaging, the elastic recovery result was unable to be quantified and was not conclusive at this point. The cross linking agents, sulphur and zinc oxide, and the accelerator agent, played a significant role in the mechanical strength of the gloves. Increment of these chemicals result in higher tensile strength, but a reduction in the elasticity of the materials in which causes a lesser elongation at break percentage for the gloves. Both cross-linkers demonstrate different behaviour where higher sulphur content, provide higher stress relaxation (SR%) yet zinc oxide shows otherwise.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.