Reconstruction of large bone defects is limited by insufficient vascularization and slow bone regeneration. The objective of this work was to investigate the effect of spatial and temporal release of recombinant human bone morphogenetic protein-2 (BMP2) and vascular endothelial growth factor (VEGF) on the extent of osteogenic and vasculogenic differentiation of human mesenchymal stem cells (hMSCs) and endothelial colony-forming cells (ECFCs) encapsulated in a patterned hydrogel. Nanogels (NGs) based on polyethylene glycol (PEG) macromers chain-extended with short lactide (L) and glycolide (G) segments were used for grafting and timed-release of BMP2 and VEGF. NGs with 12 kDa PEG molecular weight (MW), 24 LG segment length, and 60/40 L/G ratio (P12-II, NG(10)) released the grafted VEGF in 10 days. NGs with 8 kDa PEG MW, 26 LG segment length, and 60/40 L/G ratio (P8-I, NG(21)) released the grafted BMP2 in 21 days. hMSCs and NG-BMP2 were encapsulated in a patterned matrix based on acrylate-functionalized lactide-chain-extended star polyethylene glycol (SPELA) hydrogel and microchannel patterns filled with a suspension of hMSCs+ECFCs and NG-VEGF in a crosslinked gelatin methacryloyl (GelMA) hydrogel. Groups included patterned constructs without BMP2/VEGF (None), with directly added BMP2/VEGF, and NG-BMP2/NG-VEGF. Based on the results, timed-release of VEGF in the microchannels in 10 days from NG(10) and BMP2 in the matrix in 21 days from NG(21) resulted in highest extent of osteogenic and vasculogenic differentiation of the encapsulated hMSCs and ECFCs compared to direct addition of VEGF and BMP2. Further, timed-release of VEGF from NG(10) in hMSC+ECFC encapsulating microchannels and BMP2 from NG(21) in hMSC encapsulating matrix sharply increased bFGF expression in the patterned constructs. The results suggest that mineralization and vascularization are coupled by localized secretion of paracrine signaling factors by the differentiating hMSCs and ECFCs.
Current tissue engineering approaches to regeneration of articular cartilage rarely restore the tissue to its normal state because the generated tissue lacks the intricate zonal organization of the native cartilage. Zonal regeneration of articular cartilage is hampered by the lack of knowledge for the relation between physical, mechanical, and biomolecular cues and zone-specific chondrogenic differentiation of progenitor cells. This work investigated in 3D the effect of TGF-β1, zone-specific growth factors, optimum matrix stiffness, and adding nanofibers on the expression of chondrogenic markers specific to the superficial, middle, and calcified zones of articular cartilage by the differentiating human mesenchymal stem cells (hMSCs). Growth factors included BMP-7, IGF-1, and hydroxyapatite (HA) for the superficial, middle, and calcified zones, respectively; optimum matrix stiffness was 80 kPa, 2.1 MPa, and 320 MPa; and nanofibers were aligned horizontal, random, and perpendicular to the gel surface. hMSCs with zone-specific cell densities were encapsulated in engineered hydrogels and cultured with or without TGF-β1, zone-specific growth factor, optimum matrix modulus, and fiber addition and cultured in basic chondrogenic medium. The expression of encapsulated cells was measured by mRNA, protein, and biochemical analysis. Results indicated that zone-specific matrix stiffness had a dominating effect on chondrogenic differentiation of hMSCs to the superficial and calcified zone phenotypes. Addition of aligned nanofibers parallel to the direction of gel surface significantly enhanced expression of Col II in the superficial zone chondrogenic differentiation of hMSCs. Conversely, biomolecular factor IGF-1 in combination with TGF-β1 had a dominating effect on the middle zone chondrogenic differentiation of hMSCs. Results of this work could potentially lead to the development of multilayer grafts mimicking the zonal organization of articular cartilage.
The objective of this work was to synthesize an injectable and photopolymerizable hydrogel based on keratin extracted from poultry feather for encapsulation and delivery of stem cells in tissue regeneration. Since feather keratin is rich in cysteine residue, allylation of sulfhydryl groups was used for functionalization of keratin. Keratin was extracted from feather barbs by reducing the disulfide bonds in cysteine residues to sulfhydryl groups (-SH). Next, the free thiol groups were converted to dehydroalanine (Dha) by oxidative elimination using O-(2,4,6-trimethylbenzenesulfonyl) hydroxylamine. Then, the Dha moieties were converted to s-allyl cysteine by reaction with allyl mercaptan to produce keratin allyl thioether (KeratATE) biopolymer. Human mesenchymal stem cell (hMSCs) were suspended in the aqueous solution of KeratATE, injected into a mold, and photopolymerized to generate a KeratATE hydrogel encapsulating hMSCs. The freeze-dried photo-cross-linked KeratATE hydrogels had a porous, interconnected, honeycomb microstructure with pore sizes in the 20-60 μm range. The compressive modulus of the hydrogels ranged from 1 to 8 kPa depending on KeratATE concentration. KeratATE hydrogels had <5% mass loss in collagenase solution after 21 days of incubation, whereas the mass loss was 15% in trypsin solution. Degradation of KeratATE hydrogel was strongly dependent on trypsin concentration but independent of collagenase. hMSCs proliferated and adopted an elongated spindle-shape morphology after seeding on KeratATE hydrogel. KeratATE hydrogel supported differentiation of the encapsulated hMSCs to the osteogenic and chondrogenic lineages to the same extent as those hMSCs encapsulated in gelatin methacryloyl hydrogel. The results suggest that keratin allyl thioether hydrogel with controllable degradation is a viable matrix for encapsulation and delivery of stem cells in tissue regeneration.
Carboxylate-rich organic acids play an important role in controlling the growth of apatite crystals and the extent of mineralization in the natural bone. The objective of this work was to investigate the effect of organic acids on calcium phosphate (CaP) nucleation on nanofiber microsheets functionalized with a glutamic acid peptide and osteogenic differentiation of human mesenchymal stem cells (hMSCs) seeded on the CaP-nucleated microsheets. High molecular weight poly(dl-lactide) (DL-PLA) was mixed with low molecular weight L-PLA conjugated with Glu-Glu-Gly-Gly-Cys peptide, and the mixture was electrospun to generate aligned nanofiber microsheets. The nanofiber microsheets were incubated in a modified simulated body fluid (mSBF) supplemented with different organic acids for nucleation and growth of CaP crystals on the nanofibers. Organic acids included citric acid (CA), hydroxycitric acid (HCA), tartaric acid (TART), malic acid (MA), ascorbic acid (AsA), and salicylic acid (SalA). HCA microsheets had the highest CaP content at 240 ± 10% followed by TART and CA with 225 ± 8% and 225 ± 10%, respectively. The Ca/P ratio and percent crystallinity of the nucleated CaP in TART microsheets was closest to that of stoichiometric hydroxyapatite. The extent of CaP nucleation and growth on the nanofiber microsheets depended on the acidic strength and number of hydrogen-bonding hydroxyl groups of the organic acids. Compressive modulus and degradation of the CaP nucleated microsheets were related to percent crystallinity and CaP content. Osteogenic differentiation of hMSCs seeded on the microsheets and cultured in osteogenic medium increased only for those microsheets nucleated with CaP by incubation in CA or AsA-supplemented mSBF. Further, only CA microsheets stimulated bone nodule formation by the seeded hMSCs.
The objective of this work was to investigate the effect of devitalized human mesenchymal stem cells (hMSCs) and endothelial colony-forming cells (ECFCs) seeded on mineralized nanofiber microsheets on protein release, osteogenesis, vasculogenesis, and macrophage polarization. Calcium phosphate nanocrystals were grown on the surface of aligned, functionalized nanofiber microsheets. The microsheets were seeded with hMSCs, ECFCs, or a mixture of hMSCs+ECFCs, cultured for cell attachment, differentiated to the osteogenic or vasculogenic lineage, and devitalized by lyophilization. The release kinetic of total protein, bone morphogenetic protein-2 (BMP2), and vascular endothelial growth factor (VEGF) from the devitalized microsheets was measured. Next, hMSCs and/or ECFCs were seeded on the devitalized cell microsheets and cultured in the absence of osteo-/vasculo-inductive factors to determine the effect of devitalized cell microsheets on hMSC/ECFC differentiation. Human macrophages were seeded on the microsheets to determine the effect of devitalized cells on macrophage polarization. Based on the results, devitalized undifferentiated hMSC and vasculogenic-differentiated ECFC microsheets had highest sustained release of BMP2 and VEGF, respectively. The devitalized hMSC microsheets did not affect M2 macrophage polarization while vascular-differentiated, devitalized ECFC microsheets did not affect M1 polarization. Both groups stimulated higher M2 macrophage polarization compared to M1.
Resumo: An in vitro encapsulation platform utilizing hydrogels and bone matrix (BM) scaffolds to investigate the effects of microenvironmental parameters on encapsulated goat mesenchymal stem cells (gMSC) was presented. The base encapsulation matrix was composed of a biocompatible hydrogel formed through a photoinitiated polymerization process. Different polymer concentrations were used to compare the effects of hydrogel crosslinking density on physical properties, as well as on cell viability. The potential of BM to support the growth and differentiation of gMSC was also analyzed. Both methods were compared in order to analyze viability. Structures that better allow flow of oxygen showed more promising results, whereas BM structures require a better evaluation method for concrete results.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.