Background: To assess the relationship between mechanical wear and the failure of the internal lengthening mechanism in retrieved MAGnetic Expansion Control (MAGEC) growing rods. Methods: This study included 34 MAGEC rods retrieved from 20 patients. The state of the internal mechanism and mechanical wear were assessed in all the rods using plain radiographs and visual inspection. Metrology was then performed to assess the topography and mechanical wear of the telescopic bars, using a Talyrond 365 (Taylor Hobson, Leicester, UK) roundness measuring machine. Results: Plain radiographs showed evidence of a broken internal mechanism in 29% of retrieved rods. Single-side wear marks were found in 97% of retrieved rods. Material loss was found to significantly increase in rods with a damaged internal mechanism (p < 0.05) and rods with longer time in situ (r = 0.692, p < 0.05). Conclusions: We found an association between damage to the internal mechanism of the rods and (1) patterns of single-side longitudinal wear marks and (2) increased material loss. As the material loss was also found to increase over time of rod in situ, we emphasise the importance of early detection and revision of failed MAGEC rods in clinical practice.

Aims Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning. Methods 3D CT imaging was combined with a recently validated method of mapping bearing surface wear in retrieved hip implants. The asymmetrical stabilizing fins of Birmingham hip replacements (BHRs) allowed the co-registration of their acetabular wear maps and their computational models, segmented from CT scans. The in vivo location of edge-wear was measured within a standardized coordinate system, defined using the anterior pelvic plane. Results Edge-wear was found predominantly along the superior acetabular edge in all cases, while its median location was 8° (interquartile range (IQR) -59° to 25°) within the anterosuperior quadrant. The deepest point of these scars had a median location of 16° (IQR -58° to 26°), which was statistically comparable to their centres (p = 0.496). Edge-wear was in closer proximity to the superior apex of the cups with greater angles of acetabular inclination, while a greater degree of anteversion influenced a more anteriorly centred scar. Conclusion The anterosuperior location of edge-wear was comparable to the degradation patterns observed in acetabular cartilage, supporting previous findings that hip joint forces are directed anteriorly during a greater portion of walking gait. The further application of this novel method could improve the current definition of optimal and safe acetabular component positioning. Cite this article: Bone Joint Res 2021;10(10):639–649.

Aims The aim of this study was to present the first retrieval analysis findings of PRECICE STRYDE intermedullary nails removed from patients, providing useful information in the post-market surveillance of these recently introduced devices. Methods We collected ten nails removed from six patients, together with patient clinical data and plain radiograph imaging. We performed macro- and microscopic analysis of all surfaces and graded the presence of corrosion using validated semiquantitative scoring methods. We determined the elemental composition of surface debris using energy dispersive x-ray spectroscopy (EDS) and used metrology analysis to characterize the surface adjacent to the extendable junctions. Results All nails were removed at the end of treatment, having achieved their intended lengthening (20 mm to 65 mm) and after regenerate consolidation. All nails had evidence of corrosion localized to the screw holes and the extendable junctions; corrosion was graded as moderate at the junction of one nail and severe at the junctions of five nails. EDS analysis showed surface deposits to be chromium rich. Plain radiographs showed cortical thickening and osteolysis around the junction of six nails, corresponding to the same nails with moderate – severe junction corrosion. Conclusion We found, in fully united bones, evidence of cortical thickening and osteolysis that appeared to be associated with corrosion at the extendable junction; when corrosion was present, cortical thickening was adjacent to this junction. Further work, with greater numbers of retrievals, is required to fully understand this association between corrosion and bony changes, and the influencing surgeon, implant, and patient factors involved. Cite this article: Bone Jt Open 2021;2(8):599–610.

Accurate quantification of bearing material loss from retrieved metal-on-metal (MOM) hip replacements is key to understanding their failure. Geometric methods are currently the only means of estimating volumetric wear from retrieved implants and numerous contrasting approaches to obtain these measures have been published. Data collection strategies have been thoroughly discussed and refined to minimise the effect of error incurring factors; however, there is an opportunity to optimise the current methods of estimating the pre-wear geometry and, therefore, improve the accuracy of wear volume measurements. An automated analysis strategy to quantify volumetric wear is proposed in this study, which utilises the entire bearing surface to determine the implants pristine geometry. This involves the iterative removal of geometrically effected data points to optimise the fit and size of a perfect sphere. Once fitted, this reference geometry is compared with the measured data, in its entirety, to calculate the volume change representative of the quantity of material lost. Improving the reliability of this parameter could influence the care of a million patients that remain with MOM hip implants. Rigorous validation of this method will dominate future work, ensuring that the accuracy and reliability of this approach are sufficient to provide clinically meaningful data.