The FE analysis confirmed the ability of the functionally graded post to dissipate stress from the coronal to the apical end. Hence actual (physical) C-G/PEI posts could permit optimization of stress distributions in endodontically treated anterior teeth.

No abstract

The aim of the current work was to analyze the influence of the ferrule effect for hybrid composite endodontic post designs consisting of carbon (C) and glass (G) fiber-reinforced polyetherimide (PEI), in upper canine teeth. Starting from theoretical designs of C-G/PEI hybrid composite posts with different Young’s moduli (Post A—57.7 GPa, Post B—31.6 GPa, Post C—graduated from 57.7 to 9.0 GPa in the coronal–apical direction) in endodontically treated anterior teeth, the influence of the ferrule effect was determined through finite element analysis (FEA). On the surface of the crown, a load of 50 N was applied at 45° to the longitudinal axis of the tooth. Maximum principal stresses were evaluated along the C-G/PEI post as well as at the interface between the surrounding tooth structure and the post. Maximum stress values were lower than those obtained for the corresponding models without a ferrule. The presence of a ferrule led to a marked decrease of stress and gradients especially for posts A and B. A less marked effect was globally found for Post C, except in a cervical margin section along a specific direction, where a significant decrease of the stress was probably due to local geometric features, compared to the model without a ferrule. The presence of a ferrule did not generally provide a marked benefit in the case of the graduated Post C, in comparison to other C-G/PEI posts. The outcomes suggest how such a hybrid composite post alone should be sufficient to optimize the stress distribution, dissipating stress from the coronal to the apical end.

No abstract

Mechanical and architectural features play an important role in designing biomedical devices. The use of materials (i.e., Ti6Al4V) with Young's modulus higher than those of natural tissues generally cause stress shielding effects, bone atrophy, and implant loosening. However, porous devices may be designed to reduce the implant stiffness and, consequently, to improve its stability by promoting tissue ingrowth. If porosity increases, mass transport properties, which are crucial for cell behavior and tissue ingrowth, increase, whereas mechanical properties decrease. As reported in the literature, it is always possible to tailor mass transport and mechanical properties of additively manufactured structures by varying the architectural features, as well as pore shape and size. Even though many studies have already been made on different porous structures with controlled morphology, the aim of current study was to provide only a further analysis on Ti6Al4V lattice structures manufactured by selective laser melting. Experimental and theoretical analyses also demonstrated the possibility to vary the architectural features, pore size, and geometry, without dramatically altering the mechanical performance of the structure.

3D evaluation of the maxillary arch and palate highlighted significant differences between BDC and non-BDC mixed dentition subjects. Maxillary dental arch dimensions and palate morphology may allow early identification and prevention of maxillary canine impaction.

No abstract

Over the last three decades, it has been frequently reported that the properties of dental restorative composites cured with argon laser are similar or superior to those achieved with conventional halogen and light emitting diode (LED) curing units. Whereas laser curing is not dependent on the distance between the curing unit and the material, such distance represents a drawback for conventional curing units. However, a widespread clinical application of this kind of laser remains difficult due to cost, heavy weight, and bulky size. Recently, with regard to the radiation in the blue region of the spectrum, powerful solid-state lasers have been commercialized. In the current research, CAD (computer-aided design)/CAM (computer-aided manufacturing) assisted solid-state lasers were employed for curing of different dental restorative composites consisting of micro- and nanoparticle-reinforced materials based on acrylic resins. Commercial LED curing units were used as a control. Temperature rise during the photopolymerisation process and bending properties were measured. By providing similar light energy dose, no significant difference in temperature rise was observed when the two light sources provided similar intensity. In addition, after 7 days since curing, bending properties of composites cured with laser and LED were similar. The results suggested that this kind of laser would be suitable for curing dental composites, and the curing process does not suffer from the tip-to-tooth distance.