The high Young's modulus of titanium with respect to that one of the bone is the main cause of the stressshielding phenomenon, which promotes bone resorption around implants. Development of implants with a low Young's modulus has gained increased importance during the last decade, and the manufacturing of porous titanium is one of the routes to reduce this problem. In this work, porous samples of commercially pure titanium grade IV obtained by powder metallurgy with ammonium bicarbonate (NH 4 HCO 3 ) as space-holder were studied. Evaluations of porosity and mechanical properties were used to determine the influence of compaction pressure for a fixed NH 4 HCO 3 content. Measurements by ultrasound tests gave Young's modulus results that were low enough to reduce stress shielding, whilst retaining suitable mechanical strength. Biological tests on porous cp Ti showed good adhesion of osteoblasts inside the pores, which is an indicator of potential improvement of osteointegration.
Surface-associated bacterial communities, known as biofilms, are responsible for a broad spectrum of infections in humans. Recent studies have indicated that surfaces containing nanoscale protrusions, like those in dragonfly wings, create a hostile niche for bacterial colonization and biofilm growth. This functionality has been mimicked on metals and semiconductors by creating nanopillars and other high aspect ratio nanostructures at the interface of these materials. However, bactericidal topographies have not been reported on clinically relevant hydrogels and highly compliant polymers, mostly because of the complexity of fabricating nanopatterns in hydrogels with precise control of the size that can also resist aqueous immersion. Here, we report the fabrication of bioinspired bactericidal nanostructures in bacterial cellulose (BC) hydrogels using low-energy ion beam irradiation. By challenging the currently accepted view, we show that the nanostructures grown in BC affect preferentially stiff membranes like those of the Gram-positive bacteria Bacillus subtilis in a time-dependent manner and, to a lesser extent, the more deformable and softer membrane of Escherichia coli. Moreover, the nanostructures in BC did not affect the viability of murine preosteoblasts. Using single-cell analysis, we demonstrate that indeed B. subtilis requires less force than E. coli to be penetrated by nanoprobes with dimensions comparable to those of the nanostructured BC, providing the first direct experimental evidence validating a mechanical model of membrane rupture via a tension-induced mechanism within the activation energy theory. Our findings bridge the gap between mechano-bactericidal surfaces and low-dimensional materials, including single-walled carbon nanotubes and graphene nanosheets, in which a higher bactericidal activity toward Gram-positive bacteria has been extensively reported. Our results also demonstrate the ability to confer bactericidal properties to a hydrogel by only altering its topography at the nanoscale and contribute to a better understanding of the bacterial mechanobiology, which is fundamental for the rational design bactericidal topographies.
Current treatments for brain aneurysms are invasive, traumatic, and not suitable in most patients with increased risks. A new alternative method is using scaffold stents to create a local and focal attraction force of cells for an in situ reconstruction of the tunica media. For this purpose, a nanostructured bioactive coating is designed to render an asymmetric region of the stent scaffold magnetic and biomimetic, which utilizes bacterial nanocellulose (BNC) as a platform for both magnetic and cell attraction as well as proliferation. The magnetization of the BNC is realized through the reaction of Fe III and II, precipitating superparamagnetic iron oxide nanoparticles (SPION). Subsequently, magnetic bacterial nanocellulose (MBNC) is coated with polyethylene glycol to improve its biocompatibility. Cytotoxicity and biocompatibility are evaluated using porcine aortic smooth muscle cells. Preliminary cellular migration assays demonstrate the behavior between MBNC and cells labeled with SPION. In this work, (1) synthesis of BNC impregnated with magnetic nanoparticles is successfully demonstrated; (2) a viable, resilient, and biocompatible hydrogel membrane is tested for neuroendovascular application using a stent scaffold; (3) cell viability and minimal cytotoxicity is achieved; (4) cell migration tests and examination of cellular magnetic attraction confirm the viability of MBNC as a multifunctional coating.
Hydrogels provide a solution-mimicking environment for the interaction with living systems that make them desirable for various biomedical and technological applications. Because relevant biological processes in living tissues occur at the biomolecular scale, hydrogel nanopatterning can be leveraged to attain novel material properties and functionalities. However, the fabrication of high aspect ratio (HAR) nanostructures in hydrogels capable of self-standing in aqueous environments, with fine control of the size and shape distribution, remains challenging. Here, we report the synthesis of nanostructures with a HAR in bacterial cellulose (BC) hydrogel via directed plasma nanosynthesis using argon ions. The nanostructures in BC are reproducible, stable to sterilization, and liquid immersion. Using in-situ surface characterization and semiempirical modeling, we discovered that pattern formation was linked to the formation of graphitelike clusters composed of a mixture of C-C and C=C bonds. Moreover, our model predicts that reactive species at the onset of the argon irradiation accelerate the bond breaking of weak bonds, contributing to the formation of an amorphous carbon layer and nanopattern growth.
A new generation of biomaterials are evolving from being biologically inert toward bioactive surfaces, which can further interact with biological components at the nanoscale. Here, we present directed irradiation synthesis (DIS) as a novel technology to selectively apply plasma ions to bombard any type of biomaterial and tailor the nanofeatures needed for in vitro growth stimulation. In this work, we demonstrate for the first time, the influence of physiochemical cues (e.g., self-organized topography at nanoscale) of medical grade Ti6Al4V results in control of cell shape, adhesion, and proliferation of human aortic smooth muscle stem cells. The control of surface nanostructures was found to be correlated to ion-beam incidence angle linked to a surface diffusive regime during irradiation synthesis with argon ions at energies below 1 keV and a fluence of 2.5 × 1017 cm–2. Cell viability and cytoskeleton morphology were evaluated at 24 h, observing an advance cell attachment state on post-DIS surfaces. These modified surfaces showed 84% of cell biocompatibility and an increase in cytoplasmatic protusions ensuring a higher cell adhesion state. Filopodia density was promoted by a 3-fold change for oblique incidence angle DIS treatment compared to controls (e.g., no patterning) and lamellipodia structures were increased more than a factor of 2, which are indicators of cell attachment stimulation due to DIS modification. In addition, the morphology of the nanofeatures were tailored, with high fidelity control of the main DIS parameters that control diffusive and erosive regimes of self-organization. We have correlated the morphology and the influence in cell behavior, where nanoripple formation is the most active morphology for cell stimulation.
In this study, bacterial nanocellulose (BNC) produced by the bacteria Gluconacetobacter xylinus is synthesized and impregnated in situ with iron oxide nanoparticles (IONP) (Fe3O4) to yield a magnetic bacterial nanocellulose (MBNC). The synthesis of MBNC is a precise and specifically designed multi-step process. Briefly, bacterial nanocellulose (BNC) pellicles are formed from preserved G. xylinus strain according to our experimental requirements of size and morphology. A solution of iron(III) chloride hexahydrate (FeCl3·6H2O) and iron(II) chloride tetrahydrate (FeCl2·4H2O) with a 2:1 molar ratio is prepared and diluted in deoxygenated high purity water. A BNC pellicle is then introduced in the vessel with the reactants. This mixture is stirred and heated at 80 °C in a silicon oil bath and ammonium hydroxide (14%) is then added by dropping to precipitate the ferrous ions into the BNC mesh. This last step allows forming in situ magnetite nanoparticles (Fe3O4) inside the bacterial nanocellulose mesh to confer magnetic properties to BNC pellicle. A toxicological assay was used to evaluate the biocompatibility of the BNC-IONP pellicle. Polyethylene glycol (PEG) was used to cover the IONPs in order to improve their biocompatibility. Scanning electron microscopy (SEM) images showed that the IONP were located preferentially in the fibril interlacing spaces of the BNC matrix, but some of them were also found along the BNC ribbons. Magnetic force microscope measurements performed on the MBNC detected the presence magnetic domains with high and weak intensity magnetic field, confirming the magnetic nature of the MBNC pellicle. Young's modulus values obtained in this work are also in a reasonable agreement with those reported for several blood vessels in previous studies.
ResumenSe propone una nueva especie dentro del género Lasiurus a partir de 3 ejemplares recolectados en el desierto costero y vertiente occidental del sur de Perú. Basados en evidencia molecular y morfológica, Lasiurus sp. nov. está relacionada con especies rojizas del género Lasiurus (i.e., L. atratus, L. castenaeus, L. blossevillii y L. varius). La divergencia genética del gen citocromo b entre la nueva especie y las otras especies del género fueron altas (> 9.4%). Esta nueva especie, endémica de Perú, incrementa la diversidad conocida del género Lasiurus a 20 especies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.