Computer-aided design/computer-aided manufacturing (CAD/CAM) materials were submitted to thermocycling, to identify changes in mechanical behavior. Four CAD/CAM materials were divided in four subordinate groups (n=9): (1) dry out for 7 days, (2) distilled water at 37 o C for 7 days, (3) 60,000 thermocycles, and (4) 120,000 thermocycles. Following thermocycling, samples were submitted to three-point bending test. Two-way ANOVA and post-hoc Tukey's test were performed (α=0.05). The IPS e.max CAD had a flexural strength of 396±75 MPa and flexural modulus of 84±11 GPa, followed by Vita Enamic with values of 153±17 MPa and 28±5 GPa respectively. The flexural strength recorded for Lava Ultimate was 149±28 MPa and the flexural modulus was 12±3 GPa. Vitablocs Mark II had the lowest flexural strength values (125±10 MPa) and a flexural modulus of 49±15 GPa. Although polymer-based materials have similar mechanical properties compared to ceramics, they are affected by thermo cycling conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.