The performance of VMII crowns was superior to YZ crowns in the fatigue test. The premature fractures and cracks of the YZ crowns were attributed to weakness in the YZ veneer layer or in the core/veneer bond.

Objectives:The purpose of this study was to determine color changes and surface roughness of composites when they were subjected to in-office bleaching.Methods:12 discs 15 mm in diameter and 2 mm thick were prepared from two shades (A2 & A4) of two composites, Durafil VS (DF) and TPH3 (TPH). Specimens were polished and stored in distilled water for 24 hours at 37°C before being subjected to bleaching, staining, and re-bleaching. Each of the groups of specimens (DF-A2, DF-A4, TPH-A2 and TPH-A4) were subdivided into three subgroups (n=4) and bleached with Beyond, LumaWhite-Plus, and Opalescence-Boost. Specimens were then stained by immersing them in a coffee solution for 48 hours at 37°C, and then they were re-bleached. Colorimetric measurements were performed at baseline, after bleaching, after staining, and after re-bleaching. Surface roughness was determined with environmental SEM before and after bleaching. Data were statistically-analyzed.Results:None of the bleaching systems notably changed the color of composites (delta-E<2). Coffee staining affected DF specimens more than TPH. Stained specimens showed variable responses to whitening with no significant color change observed with TPH (delta-E<2) and significant changes observed with DF. Surface roughness significantly changed with bleaching, but the degree varied according to composite shade and bleaching agent.Conclusions:Three in-office bleaching agents had no significant color changes on two composites. DF showed more color change than TPH when immersed in coffee. Stained composites showed different degrees of whitening, with DF showing more response. Bleaching may adversely affect the surface texture of composites. Dentists should take into consideration that composite restorations may not respond to bleaching in the same way that natural teeth do.

No abstract

No abstract

After 1,000,000 cycles of compressive cyclic loading, PMZ composite molar crowns were more fatigue-resistant than VMII ceramic crowns. Cement type had a significant effect on fatigue resistance of the ceramic crowns but not the composite ones. Microleakage scores of ceramic crowns cemented with PAN were significantly lower than those of the other subgroups (p < 0.05).