Temperature dependence of the Vickers microhardness of BizTe2~S%2 single crystals has been studied. Loading time dependence of microhardness at different temperatures has been used for creep study in the temperature range 303 K-373 K. The activation energy for indentation creep of the crystals has been evaluated.
In the present study, europium (III) oxide (Eu O )-doped polystyrene (PS) polymer films were synthesized using a solution-casting technique for different filler levels. These films were irradiated with 5, 25 and 50 kGy γ doses and characterized using various techniques, viz. X-ray diffraction (XRD), and UV-visible and photoluminescence (PL) spectroscopies as a function of composition level and radiation dose. The UV-visible spectra indicated a decrease in the optical direct band gap of composite films with increasing concentrations of dopant and radiation dose. The band gaps of composites obtained using Tauc's equation were found to be 4.38, 4.37, 4.36 and 4.34 eV for 0, 1, 3 and 5% Eu O -doped PS respectively, while the band gaps of 5% Eu O -doped PS polymer films irradiated with 5, 25 and 50 kGy were found to be 4.30, 4.26 and 4.21 eV, respectively. Photoluminescence (PL) emission spectra showed the characteristic peaks of Eu at 595 nm, 612 nm and 617 nm with an excitation wavelength of 247 nm. The intensity of characteristic peaks of Eu was observed to increase with increasing filler concentration, while it was found to decrease with increasing radiation dose. The polymer under study may be useful in accidental dosimetry. As photoluminescence studies are carried out after a gap of 200 h from irradiation and PL emission of γ-irradiated polymer yielded 10 times emission when compared with non-irradiated polymer.
The crystals of InxBi2_xTe 3 (x = 0.1 to 0-5) have been grown by zone-melting method. In order to study anisotropy exhibited by the (0001) plane of the crystals, the directional hardness was determined by producing indentations at various azimuthal orientations of the indentor with respect to the surface over a range 0--180 °. The crystal was rotated about the indentor axis in steps of 15 ° while keeping applied load and loading time constant at 50 g and 20 sec, respectively. For annealing study, the sample was kept at a temperature of 375°C. It was observed that softening of crystal takes place and the hardness decreases to a considerable extent.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.