Surfaces of medical implants can be enhanced with the favorable properties of titanium-nitride (TiN). In a review of English medical literature, the effects of TiN-coating on orthopaedic implant material in preclinical studies were identified and the influence of these effects on the clinical outcome of TiN-coated orthopaedic implants was explored. The TiN-coating has a positive effect on the biocompatibility and tribological properties of implant surfaces; however, there are several reports of third body wear due to delamination, increased ultrahigh molecular weight polyethylene wear, and cohesive failure of the TiN-coating. This might be due to the coating process. The TiN-coating process should be optimized and standardized for titanium alloy articulating surfaces. The clinical benefit of TiN-coating of CoCrMo knee implant surfaces should be further investigated.
Autosomal dominant osteopetrosis (ADO) is a sclerotic bone disorder due to failure of osteoclasts. ADO poses difficulties during arthroplasty because of the increased chance for iatrogenic fractures due to sclerotic bone. ADO is divided into two types based on radiological findings, fracture risk, and osteoclast activity. These differences suggest less brittle bone in patients with ADO I compared to that of patients with ADO II, which suggests a smaller chance of preoperative fractures during cementless arthroplasty in ADO I compared with that in ADO II. A case of cementless total knee arthroplasty in a patient with ADO I is presented. Total hip arthroplasty was performed during follow-up, and known major problems related to ADO II were experienced. Therefore, the differences between ADO I and ADO II may not be clinically relevant for an iatrogenic fracture during arthroplasty in patients with ADO.
Titanium-nitride coating is used to improve cobalt-chromium-molybdenum implant survival in total knee arthroplasty, but its effect on osteoconduction is unknown. Chromium and cobalt ions negatively affect the growth and metabolism of cultured osteoblasts while enhancing osteoclastogenic cytokine production. Therefore, it was hypothesized that a titanium-nitride surface would enhance osteoblast proliferation and/or differentiation and reduce osteoclastogenic cytokine production compared with a cobalt-chromium-molybdenum surface. MC3T3-E1 osteoblasts showed increased proliferation and decreased differentiation on titanium-nitride, while cytokine interleukin-6 production was higher on porous cobalt-chromium-molybdenum (p < 0.05), though interleukin-1β was occasionally detected on both surfaces. These findings suggest improved osteoconduction on titanium-nitride compared with cobalt-chromium-molybdenum surface.
PurposeImprovement of biomechanical properties of cobalt–chromium–molybdenum (CoCrMo) implant surface and reduction of adhesive wear is achieved by titanium–nitride (TiN) coating in vitro. Less pain, higher postoperative outcome scores and a lower revision rate after TKA with a TiN‐coated CoCrMo TKA compared with uncoated CoCrMo TKA after 10‐year follow‐up was hypothesized.
MethodsIn a double‐blinded RCT, 101 patients received a cementless mobile‐bearing CoCrMo TKA, either TiN‐coated or uncoated. The primary outcome measure was the visual analogue scale (VAS) score for pain and secondary outcome measures were the Knee Society Score (KSS), Oxford Knee Score (OKS), revision rate and adverse events. Patients were assessed at 6 weeks, 6 months, 1 year, 5 years and 10 years, postoperatively.
Results68 patients (67%) were available for 10‐year follow‐up. No difference was found in any of the assessed outcome measures with a mean decrease in VAS score (31.6 ± 22.9) and a mean increase in OKS (10.9 ± 8.4), KSS (29.3 ± 31.4), KSSK (26.4 ± 18.2) and KSSF (4.1 ± 22.9). Overall revision rate was 7% (coated 6% vs uncoated 8%) without additional revision procedures between 5 and 10‐year follow‐up.
ConclusionsThe in vitro potential benefits of TiN coating did not result in better clinical outcome when compared to an uncoated cementless TKA. Pain, functional outcome and revision rates were comparable after 10‐year follow‐up. TiN‐coated cementless TKA provides comparable good long‐term results, similar to uncoated cementless CoCrMo TKA.
Level of evidenceLevel 1, Therapeutic Study
Netherlands Trial RegisterNL2887/NTR3033.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.