Ac ompetitive complexation strategy has been developed to construct an ovel electrocatalyst with Zn-Co atomic pairs coordinated on Nd oped carbon support (Zn/ CoN-C). Sucha rchitecture offers enhanced binding ability of O 2 ,s ignificantly elongates the O À Ol ength (from 1.23 to 1.42 ), and thus facilitates the cleavage of O À Ob ond, showing at heoretical overpotential of 0.335 Vd uring ORR process.A saresult, the Zn/CoN-C catalyst exhibits outstanding ORR performance in both alkaline and acid conditions with ah alf-wave potential of 0.861 and 0.796 Vr espectively. The in situ XANES analysis suggests Co as the active center during the ORR. The assembled zinc-air battery with Zn/CoN-Ca sc athode catalyst presents am aximum power density of 230 mW cm À2 along with excellent operation durability.T he excellent catalytic activity in acid is also verified by H 2 /O 2 fuel cell tests (peak power density of 705 mW cm À2 ).

Developing highly efficient, low-cost oxygen reduction catalysts, especially in acidic medium, is of significance toward fuel cell commercialization. Although pyrolyzed Fe-N-C catalysts have been regarded as alternatives to platinumbased catalytic materials, further improvement requires precise control of the Fe-N x structure at the molecular level and a comprehensive understanding of catalytic site structure and the ORR mechanism on these materials. In this report, we present a microporous metal−organic-framework-confined strategy toward the preferable formation of single-atom dispersed catalysts. The onset potential for Fe-N-C is 0.92 V, comparable to that of Pt/C and outperforming most noble-metal-free catalysts ever reported. A high-spin Fe 3+ -N 4 configuration is revealed by the 57 Fe Mossbauer spectrum and X-ray absorption spectroscopy for Fe L-edge, which will convert to Fe 2+ -N 4 at low potential. The in situ reduced Fe 2+ -N 4 moiety from high-spin O x -Fe 3+ -N 4 contributes to most of the ORR activity due to its high turnover frequency (TOF) of ca. 1.71 e s −1 sites −1 .

Propane dehydrogenation (PDH) has great potential to meet the increasing global demand for propylene, but the widely used Pt‐based catalysts usually suffer from short‐term stability and unsatisfactory propylene selectivity. Herein, we develop a ligand‐protected direct hydrogen reduction method for encapsulating subnanometer bimetallic Pt–Zn clusters inside silicalite‐1 (S‐1) zeolite. The introduction of Zn species significantly improved the stability of the Pt clusters and gave a superhigh propylene selectivity of 99.3 % with a weight hourly space velocity (WHSV) of 3.6–54 h−1 and specific activity of propylene formation of 65.5 molnormalC3normalH6  gPt−1 h−1 (WHSV=108 h−1) at 550 °C. Moreover, no obvious deactivation was observed over PtZn4@S‐1‐H catalyst even after 13000 min on stream (WHSV=3.6 h−1), affording an extremely low deactivation constant of 0.001 h−1, which is 200 times lower than that of the PtZn4/Al2O3 counterpart under the same conditions. We also show that the introduction of Cs+ ions into the zeolite can improve the regeneration stability of catalysts, and the catalytic activity kept unchanged after four continuous cycles.

Exploring of new catalyst activation principle holds a key to unlock catalytic powers of cheap and earth-abundant materials for large-scale applications. In this regard, the vacancy defects have been proven to be effective to initiate catalytic active sites and endow high electrocatalytic activities. However, such electrocatalytically active defects reported to date have been mostly formed by anion vacancies. Herein, it is demonstrated for the first time that iron cation vacancies induce superb water splitting bifunctionality in alkaline media. A simple wet-chemistry method is developed to grow ultrathin feroxyhyte (δ-FeOOH) nanosheets with rich Fe vacancies on Ni foam substrate. The theoretical and experimental results confirm that, in contrast to anion vacancies, the formation of rich second neighboring Fe to Fe vacancies in δ-FeOOH nanosheets can create catalytic active centers for both hydrogen and oxygen evolution reactions. The atomic level insight into the new catalyst activation principle based on metal vacancies is adaptable for developing other transition metal electrocatalysts, including Fe-based ones.

Cobalt carbide (Co2C) has recently been reported to be efficient for the conversion of syngas (CO+H2) to lower olefins (C2–C4) and higher alcohols (C2+ alcohols); however, its properties and formation conditions remain ambiguous. On the basis of our previous investigations concerning the formation of Co2C, the work herein was aimed at defining the mechanism by which the manganese promoter functions in the Co-based catalysts supported on activated carbon (CoxMn/AC). Experimental studies validated that Mn facilitates the dissociation and disproportionation of CO on the surface of catalyst and prohibits H2 adsorption to some extent, creating a relative C-rich and H-lean surface chemical environment. We advocate that the surface conditions result in the transformation from metallic Co to Co2C phase under realistic reaction conditions to form Co@Co2C nanoparticles, in which residual small Co0 ensembles (<6 nm) distribute on the surface of Co2C nanoparticles (∼20 nm). Compared with the Co/AC catalyst, where the active site is composed of Co2C phase on the surface of Co0 nanoparticles (Co2C@Co), the Mn-promoted catalysts (Co@Co2C) displayed much higher olefin selectivity (10% versus 40%), while the selectivity to alcohols over the two catalysts are similar (∼20%). The rationale behind the strong structure–performance relationship is twofold. On the one hand, Co–Co2C interfaces exist universally in the catalysts, where synergistic effects between metallic Co and Co2C phase occur and are responsible for the formation of alcohols. On the other hand, the relative C-rich and H-lean surface chemical environment created by Mn on the Co@Co2C catalysts facilitates the formation of olefins.

A competitive complexation strategy has been developed to construct a novel electrocatalyst with Zn‐Co atomic pairs coordinated on N doped carbon support (Zn/CoN‐C). Such architecture offers enhanced binding ability of O2, significantly elongates the O−O length (from 1.23 Å to 1.42 Å), and thus facilitates the cleavage of O−O bond, showing a theoretical overpotential of 0.335 V during ORR process. As a result, the Zn/CoN‐C catalyst exhibits outstanding ORR performance in both alkaline and acid conditions with a half‐wave potential of 0.861 and 0.796 V respectively. The in situ XANES analysis suggests Co as the active center during the ORR. The assembled zinc–air battery with Zn/CoN‐C as cathode catalyst presents a maximum power density of 230 mW cm−2 along with excellent operation durability. The excellent catalytic activity in acid is also verified by H2/O2 fuel cell tests (peak power density of 705 mW cm−2).

Electrochemical synthesis based on electrons as reagents provides a broad prospect for commodity chemical manufacturing. A direct one‐step route for the electrooxidation of amino C−N bonds to nitrile C≡N bonds offers an alternative pathway for nitrile production. However, this route has not been fully explored with respect to either the chemical bond reforming process or the performance optimization. Proposed here is a model of vacancy‐rich Ni(OH)2 atomic layers for studying the performance relationship with respect to structure. Theoretical calculations show the vacancy‐induced local electropositive sites chemisorb the N atom with a lone pair of electrons and then attack the corresponding N(sp3)−H, thus accelerating amino C−N bond activation for dehydrogenation directly into the C≡N bond. Vacancy‐rich nanosheets exhibit up to 96.5 % propionitrile selectivity at a moderate potential of 1.38 V. These findings can lead to a new pathway for facilitating catalytic reactions in the chemicals industry.

Bimetallic sulfides are expected to realize efficient CO 2 electroreduction into formate over aw ide potential window,however,they will undergo in situ structural evolution under the reaction conditions.T herefore,c larifying the structural evolution process,t he real active site and the catalytic mechanism is significant. Here,taking Cu 2 SnS 3 as an example, we unveiled that Cu 2 SnS 3 occurred self-adapted phase separation towardf orming the stable SnO 2 @CuS and SnO 2 @Cu 2 O heterojunction during the electrochemical process.C alculations illustrated that the strongly coupled interfaces as real active sites driven the electron self-flow from Sn 4+ to Cu + , therebypromoting the delocalized Sn sites to combine HCOO* with H*. Cu 2 SnS 3 nanosheets achieve over 83.4 %f ormate selectivity in awide potential range from À0.6 VtoÀ1.1 V. Our findings provide insight into the structural evolution process and performance-enhanced origin of ternary sulfides under the CO 2 electroreduction.