Two different configurations of photoanodes based on anodic iron oxide were investigated for photoelectrochemical water oxidation. A self-ordered and vertically oriented array of iron oxide nanotubes was obtained by anodization of pure iron substrate in an ethylene glycol based electrolyte containing 0.1M NH4F + 3 vol% water (EGWF solution) at 50 V for 15 min. Annealing of the oxide nanotubes in a hydrogen environment at 500 °C for 1 h resulted in a predominantly hematite phase. The second type of photoanode was obtained by a two-step anodization procedure. This process resulted in a two-layered oxide structure, a top layer of nano-dendrite morphology and a bottom layer of nanoporous morphology. This electrode configuration combined the better photocatalytic properties of the nano-dendritic iron oxide and better electron transportation behaviour of vertically oriented nano-channels. Annealing of these double anodized samples in an acetylene environment at 550 °C for 10 min resulted in a mixture of maghemite and hematite phases. Photocurrent densities of 0.74 mA cm−2 at 0.2 VAg/AgCl and 1.8 mA cm−2 at 0.5 VAg/AgCl were obtained under AM 1.5 illumination in 1M KOH solution. The double anodized samples showed high photoconductivity and more negative flat band potential (−0.8 VAg/AgCl), which are the properties required for promising photoanode materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.