The present study deals with the synthesis and characterization of an aliphatic copolyester, poly [butylene fumarate-co-butylene itaconate] (PIFB) copolymer was obtained from itaconic acid, fumaric acid, and 1,4-butanediol using titanium tetraisopropoxide (TTiPO) through a two step process of transesterification and melt polycondensation. The synthesized aliphatic random copolyester was characterized with the help of FT-IR,1H-NMR,13C-NMR, viscosity measurements, Gel Permeation Chromatography (GPC) and X-ray diffraction (XRD) analysis. Thermal properties have been analyzed using thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC). Hydrolytic degradation studies were carried out in acid and alkaline regions of various pH values. The synthesized copolymer was subjected toin vitroanticancer activity studies against human breast cancer (MCF-7) cell line.
Polybutylene Terephthalate (PBT) / Polycarbonate (PC) nanocomposite blend was fabricated using melt blending technique in a twin extruder. The blend composition was optimized at PBT-PC weight ratio of 80-20. The effect of incorporation of various organically modified Montmorillonite (OMMT) and naturally occurring sodium Montmorillonite (MMT) on the mechanical, thermal and morphological properties of the nanocomposites blend has been investigated. It was observed that the Izod impact strength, tensile strength and flexural strength demonstrated a significant increase with the increase in clay loading from 1-7 weight % due to homogeneous dispersion of clay within the blend matrix. Thermo gravimetric analysis (TGA) revealed an increase in thermal stability of the blend with the incorporation of nanoclay. There is also decrease in the melting temperature (Tm) and crystallisation temperature (Tc) as observed from DSC thermograms. DMA add the evidence for TGA, DSC and mechanical results. PBT -PC blend with clay exhibited featureless XRD indicative of exfoliated structure. TEM micrographs also confirm the same that the clay has exfoliated into individual layers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.