The goal of this paper is to evaluate the effectiveness of a cost-effective and eco-friendly treatment based on the use of sodium citrate (Na3C6H5O7) on the mechanical properties of flax fiber reinforced composites. To this scope, flax fibers were soaked in mildly alkaline solutions of the sodium salt at different weight concentration (i.e., 5%, 10% and 20%) for 120 h at 25 °C. The modifications on fibers surface induced by the proposed treatment were evaluated through Fourier transform infrared analysis (FTIR), whereas scanning electron microscope (SEM) and helium pycnometer were used to obtain useful information about composites morphology. The effect of the concentration of the treating solution on the mechanical response of composites was determined through quasi-static tensile and flexural tests, Charpy impact tests and dynamical mechanical thermal (DMTA) tests. The results revealed that composites reinforced with flax fibers treated in 10% solution exhibit the best mechanical performances as well as the lowest void contents. SEM analysis supported these findings showing that, by treating fibers in solutions with concentration up to 10%, composites having better morphology can be manufactured, in comparison to untreated ones. Conversely, higher Na3C6H5O7 concentrations negatively affect both the morphology and the mechanical properties of composites.
In this study, the anodizing process based on the use of tartaric sulfuric acid solution (TSA) was carried out on metal substrate to evaluate for the first time its effect on the adhesion strength and corrosion resistance of aluminium alloy (i.e., AA5083) to fibre (i.e., basalt or glass) reinforced composite adhesive joints for nautical applications. Furthermore, some TSA anodized samples were soaked in a NaOH solution to investigate the influence of this post-immersion step on the joint performances. With the aim to improve the fibre-matrix adhesion in the composite substrate thus further increasing the overall mechanical response of the joint, glass and basalt fibres were treated with a silane coupling agent solution. The corrosion behaviour of the aluminium alloy was studied by electrochemical techniques. Samples morphology was analysed by scanning electron microscopy, while the interaction between aluminium alloy substrate and epoxy resin was studied through contact angle analysis and resin uptake tests. The effectiveness of the silane treatment was examined by means of Fourier transform infrared spectroscopy and quasi-static tensile tests carried out on dry glass and basalt fabrics. The mechanical response of the resulting joints was evaluated by means of quasistatic tensile tests in accordance to ASTM D3528 standard.
This investigation aimed at developing micropatterned silica thin films (MSTFs) containing nanohydroxyapatite (nano-HA) microaggregates that were not completely covered by silica so that they could directly interact with the surrounding cells. The objectives were 1) to evaluate the effect of the presence of 2 films (MSTF with or without nano-HA addition) on the characteristic strength (σ) and Weibull modulus ( m) of a yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and 2) to evaluate the effect of these 2 films, as applied onto the Y-TZP surface, on the morphology, orientation, and proliferation of MG63 cells. Sol-gel process and soft lithography were used to apply the MSTF onto the Y-TZP specimens. Three experimental groups were produced: Y-TZP, Y-TZP + MSTF, and Y-TZP + MSTF + sprayed nano-HA. All surfaces were characterized by scanning electron microscopy and energy-dispersive X-ray spectroscopy and tested for 4-point flexural strength ( n = 30) in water at 37 °C. Weibull analysis was used to determine m and σ (maximum likelihood method). In vitro biological behavior was performed with human osteoblast-like cells (MG63). Y-TZP was successfully coated with MSFT and MSFT + nano-HA. Scanning electron microscopy micrographs indicated that the microaggregates of nano-HA were not entirely covered by the silica. There was no statistically significant difference among the experimental groups for σ and m. In the groups containing the films, the cells were elongated and aligned along the lines. The MSFT + nano-HA group showed significantly higher cell metabolic activity than that obtained for the Y-TZP group at day 7. This investigation was successful in producing an MSTF containing nano-HA microaggregates that remained exposed to the environment. The developed films did not jeopardize the structural reliability of a commercial Y-TZP, as confirmed by the Weibull statistics. The MG63 cells seeded over the films became elongated and aligned along the films' micropatterned lines. Y-TZP specimens coated with MSTF and nano-HA showed a higher cell metabolic activity and proliferation after 7 d of culture when compared with uncoated Y-TZP.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.