A magnetic force microscopy based study on the formation of stripe domains in Permalloy (Ni80Fe20) thin films is presented. Our results show that the critical thickness for stripe domain initiation depended on the sputtering rate, the substrate temperature, and the film thickness. Beyond the stripe domain formation, an increase of the period of a highly ordered array of stripe domains was evident with increasing film thickness. Thin films sputtered at room temperature with thickness variation between ∼80 and ∼350nm exhibited square-root growth dependency on stripe domains periodicity from ∼150to∼380nm, respectively. Above a certain thickness, the domain period decreased and the periodicity deteriorated with the array becoming more random, which is a strong indicator of relatively high structural perpendicular anisotropy. To illustrate, Permalloy sputtered at 100°C initially showed linear dependence in stripe domain periodicity growth up until ∼650nm thick films. The magnetic stripe domain structure began breaking down for thicker Permalloy films. Our data also suggested that the perpendicular anisotropy responsible for the formation of stripe domains might have resulted from strain-caused magnetostriction and the thin-film microstructure shape effect.
The letter reports experimental data to demonstrate magnetic force microscopy (MFM) with sub-10-nm resolution under ambient conditions. To achieve this record high resolution, multidomain states in a nanomagnetic probe were controlled. Two demagnetized (multidomain) FePt (45/55) films sputtered on a silicon probe and separated by an 8 nm thick MgO layer were further annealed at temperature of 650 °C to trigger the high-anisotropy L10 phase. A field of above 2 T was applied to drive the probes into a saturated “single-domain” state. The multidomain probes were equivalently compared with state-of-the-art conventional MFM probes via comparative imaging of benchmark magnetic recording disks.
This letter presents an experimental study that shows that a 3rd physical dimension may be used to further increase information packing density in magnetic storage devices. We demonstrate the feasibility of at least quadrupling the magnetic states of magnetic-based data storage devices by recording and reading information from nanopillars with three magnetically-decoupled layers. Magneto-optical Kerr effect microscopy and magnetic force microscopy analysis show that both continuous (thin film) and patterned triple-stack magnetic media can generate eight magnetically-stable states. This is in comparison to only two states in conventional magnetic recording. Our work further reveals that ferromagnetic interaction between magnetic layers can be reduced by combining Co/Pt and Co/Pd multilayers media. Finally, we are showing for the first time an MFM image of multilevel-3D bit patterned media with 8 discrete signal levels.
The concept of optical protein-based memory has been of interest since the early 1970s. Yet, no commercially available protein-based memory devices exist. This review presents an analysis of the main challenges associated with the practical implementation of such devices. In addition, the discussion includes details on the potential of using the unparalleled properties of photochromic proteins by creating an optical data storage disk drive with unmatched features and, particularly, record-high data densities and rates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.