The crystal structures, pyroelectric properties, and thermal stability of [111]‐oriented 0.5 mol% Mn‐doped 0.36Pb(In1/2Nb1/2)O3‐0.36Pb(Mg1/3Nb2/3)O3‐0.28PbTiO3 (Mn‐0.36PIN‐0.36PMN‐0.28PT) ternary single crystal were investigated. The temperature dependence of the Raman spectra and dielectric properties revealed that the crystal exhibited a rhombohedral (R) structure at room temperature, and ferroelectric R → tetragonal (T) and ferroelectric T to paraelectric cubic (C) phase transitions at 130 and 175°C respectively. The single crystal had a high remnant polarization of Pr = 38 μC cm–2 and coercive field of EC = 12 kV cm–1 at room temperature and a frequency of f = 100 Hz. The values of Pr and EC decreased with increasing temperature, exhibiting anomalies near their phase‐transition temperatures, which coincided with changes in the Raman spectra and dielectric properties. Furthermore, at 25°C and f = 100 Hz, the single crystal had high pyroelectric coefficients of p = 8.7 × 10−4 C m−2 K−1, figures of merit for the current responsivity of Fi = 3.5 × 10−10 m V−1, the voltage responsivity of Fv = 0.08 m2 C−1, and the detectivity of Fd = 30.1 × 10−5 Pa−1/2. These values were weakly dependent on temperature below 120°C. In addition, the room‐temperature pyroelectric coefficients of the ternary single crystal maintain over 83% of the original value at thermal annealing temperatures below 120°C. These outstanding pyroelectric properties, together with high thermal stability, indicate that [111]‐oriented rhombohedral Mn‐0.36PIN‐0.36PMN‐0.28PT ternary single crystal is a new potential candidate for infrared detection applications.
Piezoelectric and pyroelectric properties as well as strain behavior of 0.5 mol% Mn-doped 0.36Pb(In1/2Nb1/2)O3-0.36Pb(Mg1/3Nb2/3)O3-0.28PbTiO3 (Mn-PIMNT) ceramics were studied. High piezoelectric coefficient of d33 = 235 pC/N, planar electromechanical coupling factor of kp = 43.1% and the high-power Figure of Merit (FOM = 60160 pC/N) were achieved in Mn-PIMNT ceramics. Furthermore, the ceramics exhibited high pyroelectric coefficient of p = 4.8×10-4 Cm-2 K-1 , figures of merit for the current responsivity of Fi = 1.92×10-10 mV-1 , the voltage responsivity of Fv = 0.028 m 2 C-1 , and the detectivity of Fd = 2.317×10-5 Pa-1/2 at room temperature. The excellent piezoelectric and pyroelectric properties together with high ferroelectric rhombohedral to tetragonal phase transition temperature of Trt = 146 ℃ and ferroelectric tetragonal to cubic phase transition temperature of TC = 188 ℃ make the Mn-PIMNT ceramics suitable for high-temperature piezoelectric and pyroelectric devices.
Dielectric, piezoelectric, and ferroelectric properties of [001]‐oriented Mn‐0.15PIN‐0.55PMN‐0.30PT crystal are studied as functions of temperature. The single crystal exhibits excellent piezoelectric properties (d33 ~ 1330 pC N−1), higher ferroelectric to ferroelectric phase transition temperature (TR‐M ~ 112 °C), and larger coercive field (Ec ≈4.5 kV cm−1) than the binary PMN‐PT with morphotropic phase boundary compositions. Temperature‐induced phase transition characteristics of Mn‐0.15PIN‐0.55PMN‐0.30PT crystal are investigated by the temperature‐dependence Raman spectroscopy, and the temperature‐dependent electrical properties analysis shows that the values of Smax%, Q, and d33* are significantly dependent on the ferroelectric phase transitions. The results are beneficial to deeply understand the relationships between structure and properties in ternary Mn‐0.15PIN‐0.55PMN‐0.30PT single crystals.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.