No abstract

Poly(vinylidene fluoride) (PVDF) and its copolymers are the polymers with the highest dielectric constants and electroactive responses, including piezoelectric, pyroelectric and ferroelectric effects. This semicrystalline polymer can crystallize in five different forms, each related to a different chain conformation. Of these different phases, the β phase is the one with the highest dipolar moment and the highest piezoelectric response; therefore, it is the most interesting for a diverse range of applications. Thus, a variety of processing methods have been developed to induce the formation of the polymer β phase. In addition, PVDF has the advantage of being easily processable, flexible and low-cost. In this protocol, we present a number of reproducible and effective methods to produce β-PVDF-based morphologies/structures in the form of dense films, porous films, 3D scaffolds, patterned structures, fibers and spheres. These structures can be fabricated by different processing techniques, including doctor blade, spin coating, printing technologies, non-solvent-induced phase separation (NIPS), temperature-induced phase separation (TIPS), solvent-casting particulate leaching, solvent-casting using a 3D nylon template, freeze extraction with a 3D poly(vinyl alcohol) (PVA) template, replica molding, and electrospinning or electrospray, with the fabrication method depending on the desired characteristics of the structure. The developed electroactive structures have shown potential to be used in a wide range of applications, including the formation of sensors and actuators, in biomedicine, for energy generation and storage, and as filtration membranes.

Polymer‐based magnetoelectric (ME) materials are an interesting, challenging and innovative research field, that will bridge the gap between fundamental research and applications in the near future. Here, the current state of the art on the different materials, the used configurations for the development of sensors and actuators, as well as the main values of the ME coupling obtained for the different polymer‐based systems are summarized. Further, some of the specific applications that are being developed for those polymer‐based ME materials are addressed as well as the main advantages and remaining challenges in this research field.

Magnetic nanoparticles (NPs) are emerging as an important class of biomedical functional nanomaterials in areas such as hyperthermia, drug release, tissue engineering, theranostic, and lab-on-a-chip, due to their exclusive chemical and physical properties. Although some works can be found reviewing the main application of magnetic NPs in the area of biomedical engineering, recent and intense progress on magnetic nanoparticle research, from synthesis to surface functionalization strategies, demands for a work that includes, summarizes, and debates current directions and ongoing advancements in this research field. Thus, the present work addresses the structure, synthesis, properties, and the incorporation of magnetic NPs in nanocomposites, highlighting the most relevant effects of the synthesis on the magnetic and structural properties of the magnetic NPs and how these effects limit their utilization in the biomedical area. Furthermore, this review next focuses on the application of magnetic NPs on the biomedical field. Finally, a discussion of the main challenges and an outlook of the future developments in the use of magnetic NPs for advanced biomedical applications are critically provided.

No abstract

Smart and functional materials processed by printing technologies reveal an increasing interest due to small cost assembly, easy integration into devices and the possibility to obtain multifunctional materials over flexible and large areas. After introducing smart materials, printing technologies and inks, this review discusses the materials that are already being printed, mainly piezoelectric, piezoresistive, magnetostrictive, shape memory polymers (SMP), pH sensitive and chromic system materials. Since polymer-based smart materials are particularly attractive for device implementation, this review will focus on printed polymer-based smart materials. Finally, critical challenges and future research directions will be addressed.

No abstract

Magnetoelectric nanocomposite films composed of magnetostrictive CoFe 2 O 4 nanoparticles with sizes between 35 and 55 nm embedded in P(VDF-TrFE) have been successfully prepared by a solvent casting method. The ferroelectric, piezoelectric, magnetic and magnetoelectric properties of the nanocomposite and their variation with the wt% of the ferrite filler, thickness of the composite and direction of the applied magnetic field have been investigated. Ferroelectric and piezoelectric properties are improved when small amount of ferrite nanoparticles were added to the polymeric matrix. Magnetic properties vary linearity with ferrite content. The highest magnetoelectric response of 41.3 mV/cmOe was found in the composite with 72wt% when a 2.5 kOe DC field was transversely applied to the sample surface. This value is among the highest reported in two phase particulate polymer nanocomposites. Thickness of the composite has no influence in the magnetoelectric response, allowing tailoring sensor thickness for specific applications. The good value of the magnetoelectric coefficient and the flexibility of the films make these composites suitable for applications in magnetoelectric smart devices.