The kinetics of dissolution of Amazonian metakaolin in hydrochloric acid (HCl) was studied using the ‘Shrinking Core Model’ for spherical and ‘flat plate’ particles of constant size. The Amazonian kaolin was calcined at 700°C for 2 h. The calcined samples (metakaolins) were leached in an HCl solution with 5% excess at 70, 80 and 95 ± 3°C for 3 h. Samples were collected every 15 min and subjected to Al analysis by the EDTA titrimetric method. Experimental data showed that the spherical morphology produced a better fit with respect to the regression coefficients. The activation energy of the reaction was 90.6 kJ/mol. The chemical process is a first-order leaching reaction. The results of the present study are consistent with those from previous research on this topic, which used HCl with an excess of >90%.
Um estudo da reatividade e da cinética de dissolução do metacaulim foi desenvolvido para o caulim de cobertura de papel oriundo da região do Rio Capim, Pará. O caulim foi calcinado a 600, 700, 800, 900 e 1000 ºC por 2 h para obtenção do metacaulim e posteriormente lixiviado com ácido sulfúrico em temperaturas constantes dentro do intervalo 50-95 °C ± 3 °C. Nas lixiviações foram usadas quantidades de ácido sulfúrico correspondentes a 10% acima do valor estequiométrico em relação ao alumínio presente no material. Foram coletadas amostras, com intervalos pré-determinados a cada 15 min até tempo total de 3 h, as quais foram submetidas à análise de teor de alumínio pelo método titrimétrico com EDTA. Os resultados mostraram que a reatividade do caulim calcinado diminuiu com o aumento da temperatura de calcinação e que a cinética de dissolução do alumínio do metacaulim obtido por calcinação a 700 °C seguiu os métodos de reação homogênea utilizados: método integral, método das meia-vidas e método das velocidades iniciais. Uma energia de ativação de 96,25 kJ/mol foi encontrada bem como reação de lixiviação de primeira ordem em relação ao alumínio do metacaulim e de primeira ordem em relação à concentração ácida. Pesquisas realizadas anteriormente, utilizando excesso de um dos reagentes acima de 90% e modelos de reação heterogênea, estão em consonância com os dados encontrados neste trabalho desenvolvido com excesso de apenas 10%.
The kinetic study of Amazon metakaolin dissolution was performed with the application of the shrinking core model for spherical and 'flat plate' particles with constant size. The Amazon kaolin was calcinated at 700 ºC in order to produce metakaolin. This metakaolin was leached with 5% excess nitric acid at 70, 80 and 95±3 ºC for 3 h. Samples were collected every 15 min and subjected to aluminum analysis. The acid leaching was a chemically controlled process. The spherical morphology showed better fit than the flat plate particles when taking into account the regression coefficients. 91.58 kJ/mol of activation energy was found as well as an aluminum leaching reaction of the first order. The results found in this work using 5% excess acid and Amazon kaolin were consistent with previous research results using excess acid above 50% and standard kaolin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.