This study investigated the effects of different surface treatments on the repair bond strength of yttrium-stabilized tetragonal zirconia polycrystalline ceramic (Y-TZP) zirconia to a composite resin. Sixty Y-TZP zirconia specimens were prepared and randomly divided into six groups (n = 10) as follows: Group 1, surface grinding with Cimara grinding bur (control); Group 2, sandblasted with 30 µm silica-coated alumina particles; Group 3, Nd:YAG laser irradiation; Group 4, Er,Cr:YSGG laser irradiation; Group 5, sandblasted + Nd:YAG laser irradiation; and Group 6, sandblasted + Er,Cr:YSGG laser irradiation. After surface treatments, the Cimara(®) System was selected for the repair method and applied to all specimens. A composite resin was built-up on each zirconia surface using a cylindrical mold (5 × 3 mm) and incrementally filled. The repair bond strength was measured with a universal test machine. Data were analyzed using a one-way ANOVA and a Tukey HSD test (p = 0.05). Surface topography after treatments were evaluated by a scanning electron microscope (SEM). Shear bond strength mean values ranged from 15.896 to 18.875 MPa. There was a statistically significant difference between group 3 and the control group (p < 0.05). Also, a significant increase in bond strength values was noted in group 6 (p < 0.05). All surface treatment methods enhanced the repair bond strength of the composite to zirconia; however, there were no significant differences between treatment methods. The results revealed that Nd:YAG laser irradiation along with the combination of sandblasting and Er,Cr:YSGG laser irradiation provided a significant increase in bond strength between the zirconia and composite resin.
Debonding at the composite-adhesive interface is a major problem for indirect composite restorations. The aim of this study was to evaluate the bond strength (BS) of an indirect composite resin after various surface treatments (air-abrasion with Al2O3, phosphoric acid-etchig and different applications of NdYAG laser irradiations). Fifty composite disks were subjected to secondary curing to complete polymerization and randomly divided into five experimental groups (n = 10) including Group 1, untreated (control); Group 2, phosphoric acid-etched; Group 3, air-abrasion with Al2 O3 ; Group 4, Nd:YAG laser irradiated with non-contact and Group 5, Nd:YAG laser irradiated with contact. They were then bonded to resin cement and shear BS was determined in a universal testing device at a crosshead speed of 1 mm/min. One way analysis of variance (ANOVA) and Tukey post-hoc tests were used to analyze the BS values. The highest BS value was observed in Group 4 and followed by Group 3. Tukey test showed that there was no statistical difference between Group1, 2 and 5. Furthermore, differences in BSs between Group 4 and the other groups except Group 3 were significant (p < 0.05) and also there were significant differences in BSs between Group 3 to 1 and Group 3 to 2 (p < 0.05). This study reveals that air-abrasion with Al2 O3 and Nd:YAG laser irradiation with non-contact provided a significant increase in BS between indirect composite and resin cement.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.