BackgroundRecent studies have shown the potential suitability of magnesium alloys as biodegradable implants. The aim of the present study was to compare the soft tissue biocompatibility of MgCa0.8 and commonly used surgical steel in vivo.MethodsA biodegradable magnesium calcium alloy (MgCa0.8) and surgical steel (S316L), as a control, were investigated. Screws of identical geometrical conformation were implanted into the tibiae of 40 rabbits for a postoperative follow up of two, four, six and eight weeks. The tibialis cranialis muscle was in direct vicinity of the screw head and thus embedded in paraffin and histologically and immunohistochemically assessed. Haematoxylin and eosin staining was performed to identify macrophages, giant cells and heterophil granulocytes as well as the extent of tissue fibrosis and necrosis. Mouse anti-CD79α and rat anti-CD3 monoclonal primary antibodies were used for B- and T-lymphocyte detection. Evaluation of all sections was performed by applying a semi-quantitative score.ResultsClinically, both implant materials were tolerated well. Histology revealed that a layer of fibrous tissue had formed between implant and overlying muscle in MgCa0.8 and S316L, which was demarcated by a layer of synoviocyte-like cells at its interface to the implant. In MgCa0.8 implants cavities were detected within the fibrous tissue, which were surrounded by the same kind of cell type. The thickness of the fibrous layer and the amount of tissue necrosis and cellular infiltrations gradually decreased in S316L. In contrast, a decrease could only be noted in the first weeks of implantation in MgCa0.8, whereas parameters were increasing again at the end of the observation period. B-lymphocytes were found more often in MgCa0.8 indicating humoral immunity and the presence of soluble antigens. Conversely, S316L displayed a higher quantity of T-lymphocytes.ConclusionsModerate inflammation was detected in both implant materials and resolved to a minimum during the first weeks indicating comparable biocompatibility for MgCa0.8 and S316L. Thus, the application of MgCa0.8 as biodegradable implant material seems conceivable. Since the inflammatory parameters were re-increasing at the end of the observation period in MgCa0.8 it is important to observe the development of inflammation over a longer time period in addition to the present study.
The functions of some bone proteins, as osteopontin (OPN) and osteocalcin (OC), have been discovered by the latest studies. This fact suggests the possibility of their immunodetection to characterize peri-implant osteogenesis and implant impact on it. Cylindrical pins of Mg alloys (MgCa0.8, LAE442, ZEK100, LANd442) and titanium alloy (TiAl6V4) were implanted into the tibial medullae of 46 rabbits. Each group was divided regarding to implant duration (3 and 6 months). Bone samples adjacent to the implants were decalcified and treated with routine histological and immunohistochemical protocols using OC and OPN-antibodies. OC was detected in matrix of compact bone, but very rarely in osteoid and bone cells. OPN was detected intracellularly and in osteoid. After 3 months, the highest level of both markers was found in titanium group, followed by LAE442-group. In contrast to LAE442 and TiAl6V4, the other Mg alloys showed increasing levels of OC after 6 months. Lower levels of OP and OC compared to the control group are related to the continuous implant degradation and instability of bone-implant interface in early post-surgical period. Reduced marker's expression in LAE442 and TiAl6V4 groups after 6 months may indicate stabilization of bone-implant interface and completion of peri-implant neo-osteogenesis. Declining characters of OC and OPN expression over the implantation time, as well as their lowest levels in late post-surgical term, suggest a more appropriate biocompatibility of LAE442, which therefore seems to be the most preferable of the tested materials for the use in orthopaedic applications.
Biocompatibility and degradation of magnesium sponges (alloy AX30) with a fluoride (MgF(2) sponge, n = 24, porosity 63 ± 6 %, pore size 394 ± 26 μm) and with a fluoride and additional calcium-phosphate coating (CaP sponge, n = 24, porosity 6 ± 4 %, pore size 109 ± 37 μm) were evaluated over 6, 12 and 24 weeks in rabbit femurs. Empty drill holes (n = 12) served as controls. Clinical and radiological examinations, in vivo and ex vivo μ-computed tomographies and histological examinations were performed. Clinically both sponge types were tolerated well. Radiographs and XtremeCT evaluations showed bone changes comparable to controls and mild gas formation. The μCT80 depicted a higher and more inhomogeneous degradation of the CaP sponges. Histomorphometrically, the MgF(2) sponges resulted in the highest bone and osteoid fractions and were integrated superiorly into the bone. Histologically, the CaP sponges showed more inflammation and lower vascularization. MgF(2) sponges turned out to be better biocompatible and promising, biodegradable bone replacements.
Magnesium alloys are promising implant materials for use in orthopaedic applications. In the present study, screws made of the Mg-alloy ZEK100 (n = 12) were implanted in rabbit tibiae for four and six weeks, respectively. For degradation analysis, in vivo µ-computed tomography (µCT), a determination of the weight changes and SEM/EDX examinations of the screws were performed. Screw retention forces were verified by uniaxial pull-out tests. Additionally, soft-tissue biocompatibility was estimated using routine histological methods (H&E staining) and the immunohistological characterization of B- and T-cells. After six weeks, a 7.5% weight reduction occurred and, in dependence of the implant surrounding, the volume loss (µCT) reached 9.6% (screw head) and 5.0% for the part of the thread in the marrow cavity. Pull-out forces significantly decreased to 44.4% in comparison with the origin value directly after implantation. Soft tissue reactions were characterized by macrophage and lymphocyte infiltration, whereas T-cells as well as B-cells could be observed. In comparison to MgCa0.8-screws, the degradation rate and inflammatory tissue response were increased and the screw holding power was decreased after six weeks. In conclusion, ZEK100-screws seem to be inferior to MgCa0.8-screws, although their initial strength was more appropriate.
BackgroundMagnesium alloys as biodegradable implant materials received much interest in recent years. It is known that products of implant degradation can induce several types of immune response. Hence, the aim of this study was to examine the morphological changes of efferent lymph nodes after implantation of different resorbable magnesium alloys (MgCa0.8, LAE442) in comparison to commercially available resorbable (PLA) and non-resorbable (titanium) implant materials as well as control groups without implant material.MethodsThe different implant materials were inserted intramedullary into the rabbit tibia. After postoperative observation periods of three and six months, popliteal lymph nodes were examined histologically and immunhistologically and compared to lymph nodes of sham operated animals and animals without surgery. Haematoxylin and eosin staining was performed for cell differentiation. Mouse anti-CD79α and rat anti-CD3 monoclonal primary antibodies were used for B- and T-lymphocyte detection, mouse anti-CD68 primary antibodies for macrophage detection. Evaluation of all sections was performed applying a semi quantitative score.ResultsThe histological evaluation demonstrated low and moderate levels of morphological changes for both magnesium alloys (LAE442 and MgCa0.8). Higher than moderate values were reached for titanium in sinus histiocytosis and histiocytic apoptosis (3 months) and for PLA in histiocytic apoptosis (3 and 6 months). The immune response to all investigated implants had a non-specific character and predominantly was a foreign-body reaction. LAE442 provoked the lowest changes which might be due to a lower degradation rate in comparison to MgCa0.8. Therewith it is a promising candidate for implants with low immunogenic potential.ConclusionBoth examined magnesium alloys did not cause significantly increased morphological changes in efferent lymph nodes in comparison to the widely used implant materials titanium and PLA. LAE442 induced even lower immunological reactions. Therewith MgCa0.8 and especially LAE442 are appropriate candidates for biomedical use.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.