In order to expand the mechanical and physical capabilities of 3D-printed structures fabricated via commercially available 3D printers, nanocomposite and microcomposite filaments were produced via melt extrusion, 3D-printed and evaluated. The scope of this work is to fabricate physically and mechanically improved nanocomposites or microcomposites for direct commercial or industrial implementation while enriching the existing literature with the methodology applied. Zinc Oxide nanoparticles (ZnO nano) and Zinc Oxide micro-sized particles (ZnO micro) were dispersed, in various concentrations, in Acrylonitrile Butadiene Styrene (ABS) matrices and printable filament of ~1.75mm was extruded. The composite filaments were employed in a commercial 3D printer for tensile and flexion specimens’ production, according to international standards. Results showed a 14% increase in the tensile strength at 5% wt. concentration in both nanocomposite and microcomposite materials, when compared to pure ABS specimens. Furthermore, a 15.3% increase in the flexural strength was found in 0.5% wt. for ABS/ZnO nano, while an increase of 17% was found on 5% wt. ABS/ZnO micro. Comparing the two composites, it was found that the ABS/ZnO microcomposite structures had higher overall mechanical strength over ABS/ZnO nanostructures.
Rutile titanium oxide (TiO 2 ) thin films require more energy to crystallize than the anatase phase of TiO 2 . It is a prime candidate for micro-optoelectronics and is usually obtained either by high substrate temperature, applying a substrate bias, pulsed gas flow to modify the pressure, or ex situ annealing. In the present work, we managed to obtain high enough energy at the substrate in order for the particles to form rutile TiO 2 at room temperature without any intentional substrate bias in a continuous gas flow. The rutile TiO 2 thin films were deposited by a reactive radiofrequency magnetron sputtering system from a titanium target, in an argon/oxygen gas mixture. Investigations regarding the film's structure and morphology were performed by X-ray diffraction (XRD), X-ray reflectivity (XRR), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDAX), while the optical properties were investigated by means of ellipsometry.
A new approach regarding the development of nanostructured V2O5 electrochromic thin films at low temperature (250 °C), using air-carrier spray deposition and ammonium metavanadate in water as precursor is presented. The obtained V2O5 films were characterized by X-ray diffraction, scanning electron microscopy and Raman spectroscopy, while their electrochromic response was studied using UV-vis absorption spectroscopy and cyclic voltammetry. The study showed that this simple, cost effective, suitable for large area deposition method can lead to V2O5 films with large active surface for electrochromic applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.