Phase-change materials based on high density polyethylene (HDPE), soft Fischer-Tropsch paraffin wax (M3), and alkali-treated wood flour (WF) were investigated. The blend and composite samples were prepared by melt mixing using a Brabender Plastograph, followed by melt pressing. They were characterized in terms of their morphology, as well as thermal, mechanical, thermomechanical, and water absorption properties. Although SEM micrographs showed some evidence of intimate contact between the WF particles and the HDPE matrix as a result of alkali treatment, poor filler dispersion, and interfacial adhesion were also observed. Partial immiscibility of the HDPE and the M3 wax was noticed, with the WF particles covered by wax. There was plasticization of the HDPE matrix by the wax, as well as partial cocrystallization, inhomogeneity and uneven wax dispersion in the polymer matrix. The HDPE/WF/M3 wax composites were more homogeneous than the blends. The presence of wax reduced the thermal stability of the blends and composites. Both the presence of M3 wax and WF influenced the viscoelastic behavior of HDPE. The HDPE/M3 wax blends showed an increase in the interfacial amorphous content as the wax content increases, which resulted in the appearance of a b-relaxation peak. The presence of M3 wax in HDPE reduced the mechanical properties of the blends. For the composites these properties varied with WF content. An increase in wax content resulted to a decrease in water uptake by the composites, probably because the wax covered the WF particles and penetrated the pores in these particles. V C 2010 Wiley Periodicals, Inc. J Appl Polym Sci 118: [1541][1542][1543][1544][1545][1546][1547][1548][1549][1550][1551] 2010

This work reports on the effect of expandable graphite (EG) on the morphology, thermal and dynamic mechanical properties of flame retardant poly(lactic acid) (PLA)/EG composites. The composites were prepared by melt-mixing and their structure, morphology, melting and crystallization behaviour, as well as their dynamic mechanical properties, were investigated. It was found that graphite layers still existed in an aggregate structure with poor filler dispersion resulting in a lack of interfacial adhesion between EG and the PLA matrix. The presence of EG did not favour the crystallization of PLA, increased the glass transition temperature and showed a reduction in the crystallinity of the composites. The composites with higher filler contents showed enhanced storage and loss moduli. The glass transition temperatures from the loss modulus and damping factor curves varied inconsistently with EG content. The use of commercial EG as filler in PLA can preserve the thermal properties of injection moulding grade Cereplast PLA.

No abstract