The dynamic response of E-glass/epoxy composite laminates under low velocity impact was experimentally investigated. Uni-directionally reinforced E-glass/epoxy laminates with the stacking sequence of [0°/-45°/45°/0°/ 90°/0°/45°/-45°/0°] s were studied with the aim of an impact test. The impact tests performed at impactor mass (30 kg) for three different impact velocities (2.0, 2.5, and 3.0 m/s) were conducted with a specially developed vertical drop weight testing machine. The radius of the impactor with a semispherical nose was 12 mm. Sample plate specimens that had dimensions of 180 × 50, 180 × 100, and 180 × 150 mm were clamped from two opposite sides while the other two sides were free. The center of each plate was exposed to impact loading. The differences in the impact responses of specimens with varying width are characterized. Moreover, it was shown that the peak force increased with the increase of the width of the specimen.
The aqueous degradation of Eu2+‐activated and Dy3+‐codoped strontium aluminate (SrAl2O4:Eu2+, Dy3+, SA2‐Green) long afterglow phosphors synthesized from solid‐state reaction and coated with nanoscale metal oxide protective layers (≤12 nm) via atomic layer deposition (ALD) is investigated. Uncoated phosphor powders degrade rapidly upon water immersion and lose their green phosphorescence within 48 hours of water exposure. Postmortem investigations reveal hydration and decomposition of the SrAl2O4 phase. ALD of ~10 nm Al2O3 or ~12 nm TiO2 is found to significantly improve the powder's resistance to aqueous degradation. All ALD‐coated powders show minimal structural and chemical degradation and retain phosphoresence after 48 hours of water immersion. This enhanced durability offers a new pathway for applying long afterglow phosphors to outdoor applications like roadway markings or safety signage and for their incorporation into more eco‐friendly waterborne coatings.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.