Tandem solar cells that pair silicon with a metal halide perovskite are a promising option for surpassing the single-cell efficiency limit. We report a monolithic perovskite/silicon tandem with a certified power conversion efficiency of 29.15%. The perovskite absorber, with a bandgap of 1.68 electron volts, remained phase-stable under illumination through a combination of fast hole extraction and minimized nonradiative recombination at the hole-selective interface. These features were made possible by a self-assembled, methyl-substituted carbazole monolayer as the hole-selective layer in the perovskite cell. The accelerated hole extraction was linked to a low ideality factor of 1.26 and single-junction fill factors of up to 84%, while enabling a tandem open-circuit voltage of as high as 1.92 volts. In air, without encapsulation, a tandem retained 95% of its initial efficiency after 300 hours of operation.
Within the last years, perovskite semiconductors have been widely applied as active layers in thin film solar cells, as well as in many other opto-electronic devices such as light emitting diodes [1,2] and (photo) detectors. [3][4][5] Owing to their defect-tolerant nature and ease of fabrication from solution and/or vacuum deposition, [6] perovskites are the almost ideal candidate to be combined with already well-established commercial solar cell technologies such as monocrystalline silicon, [7] CIGS [8] but also with perovskite itself (all-perovskite tandem cells). [9] In the last few years, these properties enabled major research breakthroughs within a comparatively short time which has accelerated research on various PV technologies. For example, with respect to single-junction perovskite solar cells, the efficiency increased from 3.9% to 25.2% [10] within only 10 years and monolithic silicon/perovskite tandem cells reached up to 29.1% power conversion efficiency within an arguably even shorter Perovskite photovoltaic (PV) cells have demonstrated power conversion efficiencies (PCE) that are close to those of monocrystalline silicon cells; however, in contrast to silicon PV, perovskites are not limited by Auger recombination under 1-sun illumination. Nevertheless, compared to GaAs and mono crystalline silicon PV, perovskite cells have significantly lower fill factors due to a combination of resistive and non-radiative recombination losses. This necessitates a deeper understanding of the underlying loss mechanisms and in particular the ideality factor of the cell. By measuring the intensity dependence of the external open-circuit voltage and the internal quasi-Fermi level splitting (QFLS), the transport resistance-free efficiency of the complete cell as well as the efficiency potential of any neat perovskite film with or without attached transport layers are quantified. Moreover, intensitydependent QFLS measurements on different perovskite compositions allows for disentangling of the impact of the interfaces and the perovskite surface on the non-radiative fill factor and open-circuit voltage loss. It is found that potassium-passivated triple cation perovskite films stand out by their exceptionally high implied PCEs > 28%, which could be achieved with ideal transport layers. Finally, strategies are presented to reduce both the ideality factor and transport losses to push the efficiency to the thermodynamic limit.
Perovskite–silicon tandem solar cells offer the possibility of overcoming the power conversion efficiency limit of conventional silicon solar cells. Various textured tandem devices have been presented aiming at improved optical performance, but optimizing film growth on surface-textured wafers remains challenging. Here we present perovskite–silicon tandem solar cells with periodic nanotextures that offer various advantages without compromising the material quality of solution-processed perovskite layers. We show a reduction in reflection losses in comparison to planar tandems, with the new devices being less sensitive to deviations from optimum layer thicknesses. The nanotextures also enable a greatly increased fabrication yield from 50% to 95%. Moreover, the open-circuit voltage is improved by 15 mV due to the enhanced optoelectronic properties of the perovskite top cell. Our optically advanced rear reflector with a dielectric buffer layer results in reduced parasitic absorption at near-infrared wavelengths. As a result, we demonstrate a certified power conversion efficiency of 29.80%.
Large datasets are now ubiquitous as technology enables higher-throughput experiments, but rarely can a research field truly benefit from the research data generated due to inconsistent formatting, undocumented storage or improper dissemination. Here we extract all the meaningful device data from peer-reviewed papers on metal-halide perovskite solar cells published so far and make them available in a database. We collect data from over 42,400 photovoltaic devices with up to 100 parameters per device. We then develop open-source and accessible procedures to analyse the data, providing examples of insights that can be gleaned from the analysis of a large dataset. The database, graphics and analysis tools are made available to the community and will continue to evolve as an open-source initiative. This approach of extensively capturing the progress of an entire field, including sorting, interactive exploration and graphical representation of the data, will be applicable to many fields in materials science, engineering and biosciences.
Efficient mixed metal lead‐tin halide perovskites are essential for the development of all‐perovskite tandem solar cells, however they are currently limited by significant short‐circuit current losses despite their near optimal bandgap (≈1.25 eV). Herein, the origin of these losses is investigated, using a combination of voltage dependent photoluminescence (PL) timeseries and various charge extraction measurements. It is demonstrated that the Pb/Sn‐perovskite devices suffer from a reduction in the charge extraction efficiency within the first few seconds of operation, which leads to a loss in current and lower maximum power output. In addition, the emitted PL from the device rises on the exact same timescales due to the accumulation of electronic charges in the active layer. Using transient charge extraction measurements, it is shown that these observations cannot be explained by doping‐induced electronic charges but by the movement of mobile ions toward the perovskite/transport layer interfaces, which inhibits charge extraction due to band flattening. Finally, these findings are generalized to lead‐based perovskites, showing that the loss mechanism is universal. This elucidates the negative role mobile ions play in perovskite solar cells and paves a path toward understanding and mitigating a key loss mechanism.
Recent advancements in perovskite solar cell performance were achieved by stabilizing the α-phase of FAPbI3 in nip-type architectures. However, these advancements could not be directly translated to pin-type devices. Here, we fabricated a high-quality double cation perovskite (MA0.07FA0.93PbI3) with low bandgap energy (1.54 eV) using a two-step approach on a standard polymer (PTAA). The perovskite films exhibit large grains (∼1 μm), high external photoluminescence quantum yields of 20%, and outstanding Shockley–Read–Hall carrier lifetimes of 18.2 μs without further passivation. The exceptional optoelectronic quality of the neat material was translated into efficient pin-type cells (up to 22.5%) with improved stability under illumination. The low-gap cells stand out by their high fill factor (∼83%) due to reduced charge transport losses and short-circuit currents >24 mA cm–2. Using intensity-dependent quasi-Fermi level splitting measurements, we quantify an implied efficiency of 28.4% in the neat material, which can be realized by minimizing interfacial recombination and optical losses.
Perovskite/silicon tandem photovoltaics (PVs) promise to accelerate the decarbonization of our energy systems. Here, we present a thorough subcell diagnosis methodology to reveal deep insights into the practical efficiency limitations of state-of-the-art perovskite/silicon tandem PVs. Our subcell selective intensity-dependent photoluminescence (PL) and injection-dependent electroluminescence (EL) measurements allow independent assessment of pseudo-V OC and power conversion efficiencies (PCEs) for both subcells. We reveal identical metrics from PL and EL, which implies well-aligned energy levels throughout the entire cell. Relatively large ideality factors and insufficient charge extraction, however, cause each a fill factor penalty of about 6% (absolute). Using partial device stacks, we then identify significant losses in standard perovskite subcells due to bulk and interfacial recombination. Lastly, we present strategies to minimize these losses using triple halide (CsFAPb(IBrCl)3) based perovskites. Our results give helpful feedback for device development and lay the foundation toward advanced perovskite/silicon tandem PVs capable of exceeding 33% PCE.
Inorganic perovskite solar cells show excellent thermal stability, but the reported power conversion efficiencies are still lower than for organic–inorganic perovskites. This is mainly caused by lower open‐circuit voltages (VOCs). Herein, the reasons for the low VOC in inorganic CsPbI2Br perovskite solar cells are investigated. Intensity‐dependent photoluminescence measurements for different layer stacks reveal that n–i–p and p–i–n CsPbI2Br solar cells exhibit a strong mismatch between quasi‐Fermi level splitting (QFLS) and VOC. Specifically, the CsPbI2Br p–i–n perovskite solar cell has a QFLS–e ·VOC mismatch of 179 meV, compared with 11 meV for a reference cell with an organic–inorganic perovskite of similar bandgap. On the other hand, this study shows that the CsPbI2Br films with a bandgap of 1.9 eV have a very low defect density, resulting in an efficiency potential of 20.3% with a MeO–2PACz hole‐transporting layer and 20.8% on compact TiO2. Using ultraviolet photoelectron spectroscopy measurements, energy level misalignment is identified as a possible reason for the QFLS–e ·VOC mismatch and strategies for overcoming this VOC limitation are discussed. This work highlights the need to control the interfacial energetics in inorganic perovskite solar cells, but also gives promise for high efficiencies once this issue is resolved.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.