The germanides RE3Pt4Ge6 (RE=Y, Pr, Nd, Sm, Gd–Dy) have been synthesized by arc-melting of the elements followed by inductive annealing to improve the crystallinity and allow for structural order. The compounds have been studied by powder X-ray diffraction; additionally the structure of Y3Pt4Ge6 has been refined from single-crystal X-ray diffractometer data. It exhibits a (3+1)D modulated structure, indicating isotypism with Ce3Pt4Ge6. The crystal structure can be described as an intergrowth between YIrGe2- and CaBe2Ge2-type slabs along [100]. Temperature-dependent magnetic susceptibility measurements showed Pauli paramagnetism for Y3Pt4Ge6 and Curie-Weiss paramagnetism for Pr3Pt4Ge6 and Nd3Pt4Ge6. Sm3Pt4Ge6 exhibits van Vleck paramagnetism, while antiferromagnetic ordering at TN=8.1(1) K and TN=11.0(1) K is observed for Gd3Pt4Ge6 and Tb3Pt4Ge6, respectively.
Abstract. In order to investigate the magnetic properties of the solid solution CePt 1-x Pd x Al the individual compounds were synthesized from the elements using an arc furnace. From x = 0-0.8 the solid solution crystallizes in the orthorhombic TiNiSi-type structure (Pnma, no. 62;(721)(722) and for x = 0.9 both the TiNiSi-as well as the hexagonal ZrNiAl-type structures
The intermetallic solid solution CePd1−xAuxAl (x = 0.1–0.9) has been synthesized from the elements by arc-melting and subsequent annealing in induction followed by tube furnaces. The samples were characterized using the Guinier powder diffraction technique and the structures of the nominal compositions CeAuAl and CePd0.2Au0.8Al were refined from single crystal X-ray diffractometer data. For small values of x = 0.1–0.3, the compounds crystallize in the hexagonal ZrNiAl-type structure (space group P$‾{6}$2m), while for x = 0.5–0.9 the orthorhombic TiNiSi-type structure (space group Pnma) was observed. In both structure types, the transition metal and aluminum atoms form a complex polyanionic network with the cerium atoms filling the respective cavities. The transition metal atoms are in both cases surrounded in the shape of a tri-capped trigonal prism, the connectivity of these units, however, is different. Temperature-dependent magnetic susceptibility measurements of all compounds indicated a stable trivalent oxidation state for the cerium atoms along with antiferromagnetic ordering around TN ∼ 3 K.
High quality single crystals of Ce3Pt4Ge6 are obtained by repeated arc melting of the elements under Ar and subsequent annealing just below the melting point (2 h; slow cooling to 25 °C).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.