Background Periprosthetic bone loss is a well-documented phenomenon after uncemented total hip arthroplasty (THA); however, little is known about how bone mineral density (BMD) changes after 2 years.Patients and methods 14 patients with hip arthrosis (group A) were operated with a proximally porous-and hydroxyapatite-coated stem and followed for 10 years with DEXA, radiographs and Harris hip score (HHS). Another group of 14 patients (group B) was evaluated at 6 and 14 years using the same prosthesis and protocol.Results No stem was revised and all stems were wellfixed. At final follow-up, HHS was 97 points in group A after 10 years and 94 points in group B after 14 years. Bone mineral changes in group A were greatest in Gruen zones 1 and 7, where the losses were 31% and 26%, respectively, after 2 years on the operated side. The decrease in BMD continued after 2 years and in Gruen zone 7 it was faster than the rate of bone loss on the control side. In group B, the annual change in BMD on the operated side was not significantly different from the bone loss in group A.Interpretation Up to 14 years after implantation of a tapered uncemented stem, the BMD in the calcar region continues to decrease faster than would be expected from normal ageing.

Background and purpose — We hypothesized that an ultra-short stem would load the proximal femur in a more physiological way and could therefore reduce the adaptive periprosthetic bone loss known as stress shielding.Patients and methods — 51 patients with primary hip osteoarthritis were randomized to total hip arthroplasty (THA) with either an ultra-short stem or a conventional tapered stem. The primary endpoint was change in periprosthetic bone mineral density (BMD), measured with dual-energy x-ray absorptiometry (DXA), in Gruen zones 1 and 7, two years after surgery. Secondary endpoints were change in periprosthetic BMD in the entire periprosthetic region, i.e. Gruen zones 1 through 7, stem migration measured with radiostereometric analysis (RSA), and function measured with self-administered functional scores.Results — The periprosthetic decrease in BMD was statistically significantly lower with the ultra-short stem. In Gruen zone 1, the mean difference was 18% (95% CI: −27% to −10%). In zone 7, the difference was 5% (CI: −12% to −3%) and for Gruen zones 1–7 the difference was also 5% (CI: −9% to −2%). During the first 6 weeks postoperatively, the ultra-short stems migrated 0.77 mm more on average than the conventional stems. 3 months after surgery, no further migration was seen. The functional scores improved during the study and were similar in the 2 groups.Interpretation — Up to 2 years after total hip arthroplasty, compared to the conventional tapered stem the ultra-short uncemented anatomical stem induced lower periprosthetic bone loss and had equally excellent stem fixation and clinical outcome.

Background Periprosthetic bone loss occurs around uncemented femoral stems and may be influenced by the stem size.Patients and methods We studied 138 consecutive patients, 3 (2-7) years on average after a total hip arthroplasty operation (THA) for unilateral osteoarthritis with the Bi-Metric uncemented femoral stem. We analyzed Harris hip score and bone mineral density.Results The mean Harris hip score was 97 at followup. Bone mineral density decreased proximally by 19% in both Gruen zones 1 and 7. Bone loss in zones 1, 2, 6, and 7 was significantly associated with stem size. Distally, a small gain in bone mass was found in zones 3 and 5 for medium femoral sizes.Interpretation We found a marked proximal BMD loss, especially for the larger stems, which may be specific for this particular implant. Long-term studies should reveal whether this proximal bone loss will affect the longevity of the THA.

In this prospective, randomized, controlled trial on a new vitamin-E diffused HXLPE liner we found, compared to a conventional HXLPE liner, lower initial head penetration and lower superior and medial wear. A longer follow-up than two years is necessary to demonstrate lower overall head penetration in vitamin-E liners compared to contemporary highly cross-linked PE.

Risedronate taken once weekly for six months following total hip arthroplasty was effective in reducing periprosthetic bone resorption around an uncemented femoral stem up to one year after surgery but had no discernible effect on implant migration or clinical outcome. Future studies of bisphosphonate treatment following total hip arthroplasty should focus on clinically relevant end points such as the risks of fracture and revision arthroplasty.

Background and purposeRecent studies have shown that compared to the posterolateral approach, the anterolateral approach reduces the risk of dislocation after hip arthroplasty in patients with femoral neck fractures. We have therefore started to use the anterolateral approach on these patients and we now report the consequences of this change for the dislocation rate.Patients and methodsWe chose two 1-year time periods, 2007 (n = 199) and 2008 (n = 173), the former being before and the latter after the implementation of the anterolateral approach as the standard incision for hip arthroplasties in patients with femoral neck fractures. During 2007, 77% of the hips were operated on with the posterolateral approach and in 2008, 78% of the hips were operated on using the anterolateral approach.ResultsThe dislocation rate was reduced from 8% (16/199) in 2007 to 2% (3/173) in 2008. A multivariable logistic regression analysis showed that the posterolateral approach was the only factor associated with an increased risk of dislocation, with an odds ratio of 8 (2–35). Age, sex, ASA classification, type of arthroplasty, cognitive dysfunction, or the experience of the surgeon had no effect on the risk of dislocation.InterpretationSince most of our surgeons had earlier used the posterolateral approach when performing hip arthroplasties in patients with a femoral neck fracture, this study shows our surgical learning curve. We conclude that a collective policy change regarding surgical approach for these patients is both feasible and to be recommended, as it leads to a substantial reduction in dislocation rate.

Aims Radiostereometric analysis (RSA) studies of vitamin E-doped, highly crosslinked polyethylene (VEPE) liners show low head penetration rates in cementless acetabular components. There is, however, currently no data on cemented VEPE acetabular components in total hip arthroplasty (THA). The aim of this study was to evaluate the safety of a new cemented VEPE component, compared with a conventional polyethylene (PE) component regarding migration, head penetration, and clinical results. Patients and Methods We enrolled 42 patients (21 male, 21 female) with osteoarthritis and a mean age of 67 years (sd 5), in a double-blinded, noninferiority, randomized controlled trial. The subjects were randomized in a 1:1 ratio to receive a reverse hybrid THA with a cemented component of either argon-gas gamma-sterilized PE component (controls) or VEPE, with identical geometry. The primary endpoint was proximal implant migration of the component at two years postoperatively measured with RSA. Secondary endpoints included total migration of the component, penetration of the femoral head into the component, and patient-reported outcome measurements. Results In total, 19 control implants and 18 implants in the VEPE group were analyzed for the primary endpoint. We found a continuous proximal migration of the component in the VEPE group that was significantly higher with a difference at two years of a mean 0.21 mm (95% confidence interval (CI) 0.05 to 0.37; p = 0.013). The total migration was also significantly higher in the VEPE group, but femoral head penetration was lower. We found no difference in clinical outcomes between the groups. Conclusion At two years, this cemented VEPE component, although having a low head penetration and excellent clinical results, failed to meet noninferiority compared with the conventional implant by a proximal migration above the proposed safety threshold of RSA. The early proximal migration pattern of the VEPE component is a reason for continued monitoring, although a specific threshold for proximal migration and risk for later failure cannot be defined and needs further study. Cite this article: Bone Joint J 2019;101-B:1192–1198

Aims The primary aim of this study was to compare the wear properties of vitamin E-diffused, highly crosslinked polyethylene (VEPE) and one formulation of moderately crosslinked and mechanically annealed ultra-high molecular weight polyethylene (ModXLPE) in patients five years after primary total hip arthroplasty (THA). The secondary aim was to assess the clinical results of patients treated with VEPE by evaluating patient-reported outcome measures (PROMs), radiological evidence of fixation, and the incidence of mechanical failure. Patients and Methods A total of 208 patients (221 THAs) from four international centres were recruited into a prospective study involving radiostereometric analysis (RSA) and the assessment of clinical outcomes. A total of 193 hips (87%) were reviewed at the five-year follow-up. Of these, 136 (70%) received VEPE (vs ModXLPE) liners and 68 (35%) received ceramic (vs metal) femoral heads. PROMs and radiographs were collected preoperatively and at one, two, and five years postoperatively. In addition, RSA images were collected to measure PE wear postoperatively and at one, two, and five years after surgery. Results We observed similar bedding in one year postoperatively and wear two years postoperatively between the two types of liner. However, there was significantly more penetration of the femoral head in the ModXLPE cohort compared with the VEPE cohort five years postoperatively (p < 0.001). The only variables independently predictive of increased wear were ModXLPE (vs VEPE) liner type (β = 0.22, p = 0.010) and metal (vs ceramic) femoral head (β = 0.21, p = 0.013). There was no association between increased wear and the development of radiolucency (p = 0.866) or PROMs. No patient had evidence of osteolysis. Conclusion Five years postoperatively, patients with VEPE (vs ModXLPE) and ceramic (vs metal) femoral heads had decreased wear. The rates of wear for both liners were very low and have not led to any osteolysis or implant failure due to aseptic loosening.