Room temperature lasing from electrically pumped n-type doped Ge edge emitting devices has been observed. The edge emitter is formed by cleaving Si-Ge waveguide heterodiodes, providing optical feedback through a Fabry-Perot resonator. The electroluminescence spectra of the devices showed optical bleaching and intensity gain for wavelengths between 1660 nm and 1700 nm. This fits the theoretically predicted behavior for the n-type Ge material system. With further pulsed electrical injection of 500 kA/cm2 it was possible to reach the lasing threshold for such edge emitters. Different lengths and widths of devices have been investigated in order to maintain best gain-absorption ratios.
GeSn heterojunction photodetectors on Si substrates were grown with Sn concentration up to 4%, fabricated for vertical light incidence, and characterized. The complete layer structure was grown by means of ultra low temperature (100 °C) molecular beam epitaxy. The Sn content shifts the responsivity into the infrared, about 310 nm for the 4% Sn sample. An increase of the optical responsivity for wavelengths higher than 1550 nm can be observed with increasing Sn content. At 1600 nm, the optical responsivity is increased by more than a factor of 10 for the GeSn diode with 4% Sn in comparison to the Ge reference diode.
GeSn (Sn content up to 4.2%) photodiodes with vertical pin structures were grown on thin Ge virtual substrates on Si by a low temperature (160 °C) molecular beam epitaxy. Vertical detectors were fabricated by a double mesa process with mesa radii between 5 µm and 80 µm. The nominal intrinsic absorber contains carrier densities from below 1 · 10(16) cm(-3) to 1 · 10(17) cm(-3) for Ge reference detectors and GeSn detectors with 4.2% Sn, respectively. The photodetectors were investigated with electrical and optoelectrical methods from direct current up to high frequencies (40 GHz). For a laser wavelength of 1550 nm an increasing of the optical responsivities (84 mA/W -218 mA/W) for vertical incidence detectors with thin (300 nm) absorbers as function of the Sn content were found. Most important from an application perspective all detectors had bandwidth above 40 GHz at enough reverse voltage which increased from zero to -5 V within the given Sn range. Increasing carrier densities (up to 1 · 10(17) cm(-3)) with Sn contents caused the depletion of the nominal intrinsic absorber at increasing reverse voltages.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.