OBJECTIVE. Previous in vitro study has shown that TiF(4) varnish might reduce enamel erosion. No data regarding the effect of this experimental varnish on enamel erosion plus abrasion, however, are available so far. Thus, this in vitro study aimed to analyse the effect of TiF(4) compared with NaF varnishes and solutions, to protect against enamel erosion with or without abrasion. METHODS. Enamel specimens were pre-treated with experimental-TiF(4) (2.45% F), experimental-NaF (2.45% F), NaF-Duraphat (2.26% F), and placebo varnishes; NaF (2.26% F) and TiF(4) (2.45% F) solutions. Controls remained untreated. The erosive challenge was performed using a soft drink (pH 2.6) 4 × 90 s/day (ERO) and the toothbrushing abrasion (ERO+ABR) 2 × 10 s/day, for 5 days. Between the challenges, the specimens were exposed to artificial saliva. Enamel loss was measured profilometrically (μm). RESULTS. Kruskal-Wallis/Dunn tests showed that all fluoridated varnishes (TiF(4) -ERO:0.53 ± 0.20, ERO+ABR:0.65 ± 0.19/NaF-ERO:0.94 ± 0.18, ERO+ABR:1.74 ± 0.37/Duraphat-ERO:1.00 ± 0.37, ERO+ABR:1.72 ± 0.58) were able to significantly reduce enamel loss when compared with placebo varnish (ERO:3.45 ± 0.41/ERO+ABR:3.20 ± 0.66) (P < 0.0001). Placebo varnish, control (ERO:2.68 ± 0.53/ERO+ABR:3.01 ± 0.34), and fluoridated (NaF-ERO:2.84 ± 0.09/ERO+ABR:2.40 ± 0.21/TiF(4) -ERO:3.55 ± 0.59/ERO+ABR:4.10 ± 0.38) solutions did not significantly differ from each other. CONCLUSION. Based on the results, it can be concluded that the TiF(4) varnish seems to be a promising treatment to reduce enamel loss under mild erosive and abrasive conditions in vitro.
The aim of this study was to compare the effect of toothpastes containing TiF4, NaF, and SnF2 on tooth erosion-abrasion. Bovine enamel and dentin specimens were distributed into 10 groups (n = 12): experimental placebo toothpaste (no F); NaF (1450 ppm F); TiF4 (1450 ppm F); SnF2 (1450 ppm F); SnF2 (1100 ppm F) + NaF (350 ppm F); TiF4 (1100 ppm F) + NaF (350 ppm F); commercial toothpaste Pro-Health (SnF2—1100 ppm F + NaF—350 ppm F, Oral B); commercial toothpaste Crest (NaF—1.500 ppm F, Procter & Gamble); abrasion without toothpaste and only erosion. The erosion was performed 4 × 90 s/day (Sprite Zero). The toothpastes' slurries were applied and the specimens abraded using an electric toothbrush 2 × 15 s/day. Between the erosive and abrasive challenges, the specimens remained in artificial saliva. After 7 days, the tooth wear was evaluated using contact profilometry (μm). The experimental toothpastes with NaF, TiF4, SnF2, and Pro-Health showed a significant reduction in enamel wear (between 42% and 54%). Pro-Health also significantly reduced the dentin wear. The toothpastes with SnF2/NaF and TiF4/NaF showed the best results in the reduction of enamel wear (62–70%) as well as TiF4, SnF2, SnF2/NaF, and TiF4/NaF for dentin wear (64–79%) (P < 0.05). Therefore, the experimental toothpastes containing both conventional and metal fluoride seem to be promising in reducing tooth wear.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.