We report the growth and characterization of record‐efficiency ZnO/CdS/CuInGaSe2 thin‐film solar cells. Conversion efficiencies exceeding 19% have been achieved for the first time, and this result indicates that the 20% goal is within reach. Details of the experimental procedures are provided, and material and device characterization data are presented. Published in 2003 by John Wiley & Sons, Ltd.
Plasmon-active silver nanoparticle layers were included in solution-processed bulk-heterojunction solar cells. Nanoparticle layers were fabricated using vapor-phase deposition on indium tin oxide electrodes. Owing to the increase in optical electrical field inside the photoactive layer, the inclusion of such particle films lead to increased optical absorption and consequently increased photoconversion at solar-conversion relevant wavelengths. The resulting solar energy conversion efficiency for a bulk heterojunction photovoltaic device of poly(3-hexylthiophene)/[6,6]-phenyl C61 butyric acid methyl ester was found to increase from 1.3%±0.2% to 2.2%±0.1% for devices employing thin plasmon-active layers. Based on six measurements, the improvement factor of 1.7 was demonstrated to be statistically significant.
A photovoltaic conversion efficiency of 40.8% at 326 suns concentration is demonstrated in a monolithically grown, triple-junction III–V solar cell structure in which each active junction is composed of an alloy with a different lattice constant chosen to maximize the theoretical efficiency. The semiconductor structure was grown by organometallic vapor phase epitaxy in an inverted configuration with a 1.83 eV Ga.51In.49P top junction lattice-matched to the GaAs substrate, a metamorphic 1.34 eV In.04Ga.96As middle junction, and a metamorphic 0.89 eV In.37Ga.63As bottom junction. The two metamorphic junctions contained approximately 1×105 cm−2 and 2–3×106 cm−2 threading dislocations, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.