This study compared commercial composite resin blocks with one ceramic block for use in computer-aided design/computer aided manufacturing (CAD/CAM). Four composite resins, one composite ceramic, and one feldspar-ceramic block were investigated. Flexural strength (FS), flexural modulus (FM), and Vickers hardness (VH) were determined under three conditions: dry storage; immersion in water at 37°C for 7 days; and immersion in water at 37°C for 7 days followed by 10,000 thermocycles. After dry storage, FS ranged from 127 to 242 MPa, FM from 9.6 to 51.5 GPa, and VH from 64 to 455. Two-way ANOVA was performed for FS, FM and VH followed by Tukey's multiple comparison (α<0.05). Results demonstrated that the materials degraded after water immersion and thermocycling, but their properties were within the acceptable range for fabrication of single restorations according to the ISO standard for ceramics (ISO 6872:2008).
ObjectivesThis study evaluated color differences (ΔEs) and translucency parameter changes (ΔTPs) of various computer-aided design/computer-aided manufacturing (CAD/CAM) blocks after immersion in coffee.Materials and MethodsEight CAD/CAM blocks and four restorative composite resins were evaluated. The CIE L*a*b* values of 2.0 mm thick disk-shaped specimens were measured using the spectrophotometer on white and black backgrounds (n = 6). The ΔEs and ΔTPs of one day, one week, and one month immersion in coffee or water were calculated. The values of each material were analyzed by two-way ANOVA and Tukey's multiple comparisons (α = 0.05). The ΔEs after prophylaxis paste polishing of 1 month coffee immersion specimens, water sorption and solubility were also evaluated.ResultsAfter one month in coffee, ΔEs of CAD/CAM composite resin blocks and restorative composites ranged from 1.6 to 3.7 and from 2.1 to 7.9, respectively, and ΔTPs decreased. The ANOVA of ΔEs and ΔTPs revealed significant differences in two main factors, immersion periods and media, and their interaction except for ΔEs of TEL (Telio CAD, Ivoclar Vivadent). The ΔEs significantly decreased after prophylaxis polishing except GRA (Gradia Block, GC). There was no significant correlation between ΔEs and water sorption or solubility in water.ConclusionsThe ΔEs of CAD/CAM blocks after immersion in coffee varied among products and were comparable to those of restorative composite resins. The discoloration of CAD/CAM composite resin blocks could be effectively removed with prophylaxis paste polishing, while that of some restorative composites could not be removed.
Fluoride released for 1-year water storage will contribute to secondary caries prevention. The amount of fluoride release did not affect these mechanical properties. These results indicate the usefulness of these GICs.
Aim of this study was to investigate effects of space thickness and consistency of wash materials on sulcus depth reproduction with silicone impressions, low (L), medium (M), and very high consistency (VH), using two-step putty-wash technique. Impressions were taken from truncated cones with 50-, 100-, or 200-μm-wide sulci, using the combinations L+VH or M+VH and different space thickness for wash materials: 2 mm (ST2), 1 mm (ST1), and approximately 25 μm (ST0.025). Sulcus depth reproduction tended to increase with increasing sulcus width. Sulcus reproduction of ST0.025 was deeper than those of the other groups. At 100-and 200-μm sulcus widths, sulcus reproductions of ST1 and ST2 with L+HV were deeper than with M+HV. Regardless of consistency, the thin spacer produced deep reproduction. Adequate 0.5 mm sulcus reproductions were obtained with 100 and 200 μm wide sulci and 1-and 2-mm spacer widths, combined with low consistency impression material.
The objective of this study was to evaluate the effect of the concentration of calcium chloride (CaCl 2 ) solution on the surface hardness of restorative glass ionomer cements (GICs). Two high-viscosity GICs, Fuji IX GP and GlasIonomer FX-II, were immersed in several concentrations of CaCl 2 solution for 1 day and 1 week. The immersed specimen surfaces were evaluated using microhardness testing, grazing incidence X-ray diffraction, and energy-dispersive X-ray spectroscopy. Immersion in a higher concentration of CaCl 2 solution produced a greater increase in the surface hardness. No crystalline substance was observed on the immersed surface. Calcium ions were selectively absorbed in the matrix of the GIC surface after immersion. They reacted with the non-reacted carboxylic acid groups remaining in the cement matrix. These reactions were considered to cause an increase in the surface hardness of the GICs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.