This study compared commercial composite resin blocks with one ceramic block for use in computer-aided design/computer aided manufacturing (CAD/CAM). Four composite resins, one composite ceramic, and one feldspar-ceramic block were investigated. Flexural strength (FS), flexural modulus (FM), and Vickers hardness (VH) were determined under three conditions: dry storage; immersion in water at 37°C for 7 days; and immersion in water at 37°C for 7 days followed by 10,000 thermocycles. After dry storage, FS ranged from 127 to 242 MPa, FM from 9.6 to 51.5 GPa, and VH from 64 to 455. Two-way ANOVA was performed for FS, FM and VH followed by Tukey's multiple comparison (α<0.05). Results demonstrated that the materials degraded after water immersion and thermocycling, but their properties were within the acceptable range for fabrication of single restorations according to the ISO standard for ceramics (ISO 6872:2008).
BACKGROUND: Immobilization of phosphoproteins on type-I collagen via covalent binding may induce extra-and intrafibrillar mineralization. OBJECTIVE: This study tested the hypothesis that methacrylate phosphate esters immobilized on reconstituted type-I collagen can mimic the nucleating role of phosphoproteins. METHODS: Three functional monomers (MDP, GPDM and Phenyl-P) that differed in chemical structure and steric hindrances around the phosphate moiety were evaluated. Reconstituted type-I collagen was either left untouched (control) or treated by 5% monomer/ethanol for 20 s. All samples were incubated in simulated dentinal fluid as mineralizing medium at 37 • C for 7 or 14 days. The extra-and intrafibrillar mineralization were examined by SEM and TEM/SAED crystallography, respectively. RESULTS: FT-IR spectroscopy showed that the phosphate groups were incorporated on reconstituted collagen, irrespective of their chemical structure. MDP immobilization induced dense growth of extrafibrillar mineral over time, while with GPDMand Phenyl-P-immobilized collagen, mineralization was moderate and sparse, respectively. TEM/SAED evidence disclosed that intrafibrillar minerals exclusively occurred in MDP-immobilized collagen. CONCLUSIONS: Immobilization of MDP, which had the lowest steric hindrance, could induce significant biomimetic extraand intrafibrillar mineralization; resembling the lowest level of hierarchy organization of dentin.
The aim of the present study was to characterize the effects of the ultraviolet light (UV) irradiation period on the bond strength of fiber-reinforced composite (FRC) posts to core build-up resin. Three types of FRC posts were prepared using polymethyl methacrylate, urethane dimethacrylate, and epoxy resin. The surfaces of these posts were treated using UV irradiation at a distance of 15 mm for 0 to 600 s. The pull-out bond strength was measured and analyzed with the Dunnett's comparison test (α=0.05). The bond strengths of the post surfaces without irradiation were 6.9 to 7.4 MPa; those after irradiation were 4.2 to 26.1 MPa. The bond strengths significantly increased after 15 to 120-s irradiation. UV irradiation on the FRC posts improved the bond strengths between the FRC posts and core build-up resin regardless of the type of matrix resin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.