Aim:The aim of this study is to compare the shear bond strengths of conventional resin cement and self-adhesive resin cement bonded to lithium disilicate. Materials and methods:A total of 40 extracted human molar teeth were mounted in self-cure acrylic resin. Teeth were prepared to obtain flat occlusal surface. About 40 lithium disilicate specimens of dimension-10 mm in diameter and thickness of 2 mm-were fabricated using lost wax technique. The samples were divided into four groups: Groups I, II, III, and IV (n = 10). The specimens were surface treated with Monobond S silane coupling agent. Self-etching primer and bonding agent were applied on the bonding surface of the teeth in groups I and III. The specimens were bonded to the primed teeth with the Multilink N resin cement and subjected to the universal testing machine. The specimens were light-cured. Specimens in groups II and IV were luted to teeth using self-adhesive cement RelyX U100. The same force was applied over the specimen as mentioned above. Excess cement was removed, and light curing was done. The specimens in groups III and IV were subjected to thermocycling for 10,000 cycles at temperatures altering between 5°C and 55°C. Results:The shear bond strengths of conventional resin cement and self-adhesive resin cement with lithium disilicate were tested before and after thermocycling. Department of Pediatric and Preventive Dentistry, Sri Sankara Dental College, Thiruvananthapuram, Kerala, India Corresponding Author: Anip K Roy, Department of Prosthodontics, Purvanchal Institute of Dental Sciences Gorakhpur, Uttar Pradesh, India, e-mail: royanip86@gmail.com thermocycling has no significant effect on the bond strengths of conventional or self-adhesive resin cement. However, from the study, it is seen that conventional resin cement had a higher shear bond strength value than the self-adhesive resin cement. Conclusion:There was a significant difference between the average shear bond strength values of conventional resin cement (Multilink N) and self-adhesive resin cement (RelyX U100) when bonded to lithium disilicate disks, and thermocycling had no significant effect on the bond strength of conventional or self-adhesive resin cements.Clinical significance: Among all-ceramic systems available, lithium disilicate materials have emerged as an excellent esthetic material for fabrication of anterior and posterior crowns and three-unit anterior fixed partial dentures because of their high translucency and improved optical properties. For successful clinical outcomes, the luting agent should have high bond strength not only to the ceramic surface, but also to the tooth surface.
Background:The smear layer is an amorphous film, i.e., always formed by the action of endodontic instruments inside the root canal during chemomechanical preparation. Different solutions have been used and tested for its removal. For the removal of smear layer, demineralization, and softening of root dentin, chelating agents have been preferred.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.