Metal organic chemical vapor deposition of GaAs on standard nominal 300 mm Si(001) wafers was studied. Antiphase boundary (APB) free epitaxial GaAs films as thin as 150 nm were obtained. The APB-free films exhibit an improvement of the room temperature photoluminescence signal with an increase of the intensity of almost a factor 2.5. Hall effect measurements show an electron mobility enhancement from 200 to 2000 cm2/V s. The GaAs layers directly grown on industrial platform with no APBs are perfect candidates for being integrated as active layers for nanoelectronic as well as optoelectronic devices in a CMOS environment.
We report on the first electrically pumped continuous-wave (cw) InAs/GaAs quantum dot (QD) lasers monolithically grown on on-axis Si (001) substrates without any intermediate buffer layers. A 400 nm antiphase boundary (APB) free epitaxial GaAs film with a small root-mean-square (RMS) surface roughness of 0.86 nm was first deposited on a 300 mm standard industry-compatible on-axis Si (001) substrate by metal-organic chemical vapor deposition (MOCVD). The QD laser structure was then grown on this APB-free GaAs/Si (001) virtual substrate by molecular beam epitaxy (MBE). Room-temperature cw lasing at ~1.3 µm has been achieved with a threshold current density of 425 A/cm2 and single facet output power of 43 mW. Under pulsed operation, lasing operation up to 102 °C has been realized, with a threshold current density of 250 A/cm2 and single facet output power exceeding 130 mW at room temperature.
Semiconductor III-V photonic crystal (PC) laser is regarded as a promising ultra-compact light source with unique advantages of ultralow energy consumption and small footprint for the next generation of Si-based on-chip optical interconnects. However, the significant material dissimilarities between III-V materials and Si are the fundamental roadblock for conventional monolithic III-V-on-silicon integration technology. Here, we demonstrate ultrasmall III-V PC membrane lasers monolithically grown on CMOS-compatible on-axis Si (001) substrates by using III-V quantum dots. The optically pumped InAs/GaAs quantumdot PC lasers exhibit single-mode operation with an ultra-low threshold of~0.6 μW and a large spontaneous emission coupling efficiency up to 18% under continuous-wave condition at room temperature. This work establishes a new route to form the basis of future monolithic light sources for high-density optical interconnects in future large-scale silicon electronic and photonic integrated circuits.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.