No abstract

The aim of this study is to investigate the morphological and chemical changes of demineralized dentin collagen-matrix and resin/dentin interface associated with chitosan/riboflavin modification. Dentin disc specimens were prepared from sound molars, acid-etched with 35% phosphoric acid and modified with either 0.1% riboflavin or chitosan/riboflavin (Ch/RF ratios 1:4 or 1:1) and photo-activated by UVA. Morphological and chemical changes associated with surface modification were characterized by SEM and micro-Raman spectroscopy. Dentin surfaces of sound molars were exposed, acid-etched, and modified as described before. Etch-and-rinse dentin adhesive was applied, light-cured, and layered with resin-restorative composite. The resin infiltration and resin/dentin interface were characterized by micro-Raman spectroscopy and SEM. An open-intact collagen network-structure, formation of uniform hybrid-layer and higher resin infiltration were found with 0.1%RF and Ch/RF 1:4 modifications. Raman analysis revealed chemical changes and shifts in Amide bands with the modification of dentin collagen-matrix. The use of riboflavin and chitosan/riboflavin formulations to modify dentin-collagen matrix, with the defined ratios, stabilizes the collagen fibrillar network and enhances resin infiltration and hybrid layer formation. These preliminary results are encouraging for subsequent consideration of chitosan/riboflavin modification in adhesive dentistry.

Crosslinking is considered a possible approach to increasing the mechanical and structural stability and biodegradation resistance of the dentin collagen matrix. The aim of this study was to investigate the mechanical and chemical variations and collagen degradation resistance associated with crosslinking of the dentin collagen matrix with UVA-activated riboflavin. Dentin collagen matrix specimens were treated with 0.1 and 1% riboflavin for 2 min and photo-activated with 7 mW/cm(2) UVA (368 nm) for 2 min. The structural change of the dentin collagen network with collagenase exposure was investigated by AFM and SEM at different time-points. The variations in surface/bulk mechanical properties and biodegradation resistance were characterized by nano-indentation, conventional mechanical testing, and hydroxyproline liberation at different time-points. Chemical changes associated with riboflavin/collagen-matrix interaction were analyzed by micro-Raman spectroscopy. UVA-activated riboflavin increased the mechanical properties, mechanical stability, and biodegradation resistance of the dentin collagen matrix. Higher collagen-network structural resistance against collagenolytic challenges was found with crosslinking. micro-Raman spectroscopy showed a strong dependency, in both intensity and wave-number, of certain Raman bands (1242-1667 cm(-1)) with crosslinking indicating the collagen/riboflavin interactions. UVA-activated riboflavin (1%) more efficiently crosslinked the dentin collagen matrix within a relatively clinically acceptable time-frame compared with 0.1% riboflavin.

No abstract

Treating root dentine with PAs-rich grape seed extracts improved the biodegradation resistance of demineralized root dentine and enhanced the bond strength and durability between resin-based sealer and root dentine after short-term water storage.