Stable and rigid carbon atomic chains were experimentally realized by removing carbon atoms row by row from graphene through the controlled energetic electron irradiation inside a transmission electron microscope. The observed structural dynamics of carbon atomic chains such as formation, migration, and breakage were well explained by density-functional theory calculations. The method we reported here is promising to investigate all-carbon-based devices with the carbon atomic chains as the conducting channel, which can be regarded as the ultimate basic component of molecular devices.

Single-walled carbon nanotubes (CNTs) may enable the fabrication of integrated circuits smaller than 10 nanometers, but this would require scalable production of dense and electronically pure semiconducting nanotube arrays on wafers. We developed a multiple dispersion and sorting process that resulted in extremely high semiconducting purity and a dimension-limited self-alignment (DLSA) procedure for preparing well-aligned CNT arrays (within alignment of 9 degrees) with a tunable density of 100 to 200 CNTs per micrometer on a 10-centimeter silicon wafer. Top-gate field-effect transistors (FETs) fabricated on the CNT array show better performance than that of commercial silicon metal oxide–semiconductor FETs with similar gate length, in particular an on-state current of 1.3 milliamperes per micrometer and a recorded transconductance of 0.9 millisiemens per micrometer for a power supply of 1 volt, while maintaining a low room-temperature subthreshold swing of <90 millivolts per decade using an ionic-liquid gate. Batch-fabricated top-gate five-stage ring oscillators exhibited a highest maximum oscillating frequency of >8 gigahertz.

Large-area monolayer WS2 is a desirable material for applications in next-generation electronics and optoelectronics. However, the chemical vapour deposition (CVD) with rigid and inert substrates for large-area sample growth suffers from a non-uniform number of layers, small domain size and many defects, and is not compatible with the fabrication process of flexible devices. Here we report the self-limited catalytic surface growth of uniform monolayer WS2 single crystals of millimetre size and large-area films by ambient-pressure CVD on Au. The weak interaction between the WS2 and Au enables the intact transfer of the monolayers to arbitrary substrates using the electrochemical bubbling method without sacrificing Au. The WS2 shows high crystal quality and optical and electrical properties comparable or superior to mechanically exfoliated samples. We also demonstrate the roll-to-roll/bubbling production of large-area flexible films of uniform monolayer, double-layer WS2 and WS2/graphene heterostructures, and batch fabrication of large-area flexible monolayer WS2 film transistor arrays.