The use of MTA + metallic post as an intra-radicular reinforcement treatment increased the resistance to fracture of weakened bovine teeth in an experimental immature tooth model.

Objective:The aim of this study was to evaluate the fracture strength and failure mode of flared bovine roots restored with different intraradicular posts.Material and Methods:Fifty bovine incisors with similar dimensions were selected and their roots were flared until 1.0 mm of dentin wall remained. Next, the roots were allocated into five groups (n=10): GI-cast metal post-and-core; GII-fiber posts plus accessory fiber posts; GIII- direct anatomic post; GIV- indirect anatomic post and GV- control (specimens without intraradicular post). A polyether impression material was used to simulate the periodontal ligament. After periodontal ligament simulation, the specimens were subjected to a compressive load at a crosshead speed of 0.5 mm/min in a servo-hydraulic testing machine (MTS 810) applied at 135° to the long axis of the tooth until failure. The data (N) were subjected to ANOVA and Tukey's post-hoc test (α=0.05).Results:GI and GIV presented higher fracture strength (p<0.05) than GII. GIII presented intermediate values without statistically significant differences (p>0.05) from GI, GII and GIV. Control specimens (GV) produced the lowest fracture strength mean values (p<0.05). Despite obtaining the highest mean value, GI presented 100% of unfavorable failures. GII presented 20% of unfavorable failures. GIII, GIV and GV presented only favorable failures.Conclusions:Although further in vitro and in vivo studies are necessary, the results of this study showed that the use of direct and indirect anatomic posts in flared roots could be an alternative to cast metal post-and-core.

We have evaluated the resistance to displacement of six stable methods of fixation of a sagittal split ramus osteotomy (SSRO) in the mandibular advancement with counterclockwise rotation. We tested 60 synthetic hemimandibles in six groups of 10 each: Group I - fixation with a straight four-hole 2.0mm miniplate; Group II - a straight six-hole 2.0mm miniplate; Group III - two straight 2.0mm four-hole miniplates; Group IV - an eight-hole 2.0mm (grid plate); Group V - a 2.0mm four-hole straight miniplate and 2.0×12mm bicortical screw; and Group VI - a straight four-hole 2.0mm locking miniplate. We applied a linear force in the region between the canine and the first premolar using a universal testing machine (EMIC- DL2000) with a loading cell of 10 KN. The loads at 1, 3, and 5mm displacement were recorded (N) and the data transmitted from the load cell to a computer. Results were analysed using analysis of variance (ANOVA) (p<0.001) and the Tukey post-test for comparison of the significance of the differences between the groups. For the three degrees of displacement, fixation with two straight 2.0mm plates and with the grid plate gave higher load values.

No abstract

SPC and SP led to equal reduction on fracture resistance of dental crowns, regardless of being mixed with water or 20% HP.

Objective. To evaluate the surface roughness of IPS Empress 2 ceramic when treated with different finishing/polishing protocols.Materials and methods.Sixteen specimens of IPS Empress 2 ceramic were made from wax patterns obtained using a stainless steel split mold. The specimens were glazed (Stage 0–S0, control) and divided into two groups. The specimens in Group 1 (G1) were finished/polished with a KG Sorensen diamond point (S1), followed by KG Sorensen siliconized points (S2) and final polishing with diamond polish paste (S3). In Group 2 (G2), the specimens were finished/polished using a Shofu diamond point (S1), as well as Shofu siliconized points (S2) and final polishing was performed using Porcelize paste (S3). After glazing (S0) and following each polishing procedure (S1, S2 or S3), the surface roughness was measured using TALYSURF Series 2. The average surface roughness results were analyzed using ANOVA followed by Tukey post-hoc tests (α = 0.01)Results.All of the polishing procedures yielded higher surface roughness values when compared to the control group (S0). S3 yielded lower surface roughness values when compared to S1 and S2.Conclusions.The proposed treatments negatively affected the surface roughness of the glazed IPS Empress 2 ceramic.

Adjustments by grinding in 3Y-TZP frameworks should be performed with water cooling, and regeneration firing should be undertaken to obtain a more reliable material.

No abstract