The experimental alloys are suitable options for dental implant manufacturing, particularly the binary system, which showed a better combination of mechanical and electrochemical properties without the presence of toxic elements.
This study compared the effectiveness of Ricinus communis (RC) with Nystatin (NYS) and Miconazole (MIC) in the treatment of institutionalised elderly with denture stomatitis (DS). They (n = 30) were randomly distributed into three groups: MIC, NYS or RC. Clinical and mycological evaluations were performed prior to the use of the antifungal (baseline) and repeated after 15 and 30 days of treatment. The sample was clinically examined for oral mucosal conditions. Standard photographs were taken of the palate, and the oral candidiasis was classified (Newton's criteria). Mycological investigation was performed by swabbing the palatal mucosa, and Candida spp. were quantified by counting the number of colony-forming units (cfu mL⁻¹). The clinical and mycological data were analysed, respectively by Wilcoxon and Student's t-test (α = 0.05). Significant improvement in the clinical appearance of DS in the MIC and RC groups was observed between the 1st and 3rd collections (MIC - P = 0.018; RC - P = 0.011) as well as between the 2nd and 3rd collections (MIC - P = 0.018; RC - P = 0.011). Neither groups showed a statistically significant reduction in cfu mL⁻¹ at any time. Although none of the treatments decreased the cfu mL⁻¹, it was concluded that Ricinus communis can improve the clinical condition of denture stomatitis in institutionalised elderly patients, showing similar results to Miconazole.
Exposure to toothpastes (immersion) does not affect titanium per se; their use during brushing affects titanium topography and roughness. The associated effects of toothpaste abrasives and fluorides seem to increase roughness on titanium brushed surfaces.
Objective:This study compared the cutting capacity of carbide burs sterilized with microwaves and traditional sterilization methods.Material and Methods:Sixty burs were divided into 5 groups according to the sterilization methods: dry heat (G1), autoclave (G2), microwave irradiation (G3), glutaraldehyde (G4) or control – no sterilization (G5). The burs were used to cut glass plates in a cutting machine set for twelve 2.5-min periods and, after each period, they were sterilized (except G5) following the protocol established for each group. The cutting capacity of the burs was determined by a weight-loss method. Data were analyzed statistically by Kruskal-Wallis and Dunn's test.Results:The means of the cutting amount performed by each group after the 12 periods were G1 = 0.2167 ± 0.0627 g; G2 = 0.2077 ± 0.0231 g; G3 = 0.1980 ± 0.0326 g; G4 = 0.1203 ± 0.0459 g; G5 = 0.2642 ± 0.0359 g. There were statistically significant differences among the groups (p<0.05); only dry heat sterilization was similar to the control.Conclusion:Sterilization by dry heat was the method that least affected the cutting capacity of the carbide burs and microwave sterilization was not better than traditional sterilization methods.
Adjustments by grinding in 3Y-TZP frameworks should be performed with water cooling, and regeneration firing should be undertaken to obtain a more reliable material.
This study evaluated microstructural and crystallographic phase changes after grinding (G) and regeneration firing/anneling (R) of Y-TZP ceramics. Thirty five bars (Lava TM and Ice Zirkon) were divided: Y-TZP pre-sintered, control (C), regeneration firing (R), dry grinding (DG), dry grinding+regeneration firing (DGR), wet grinding (WG) and wet grinding+regeneration firing (WGR). Grinding was conducted using a diamond bur and annealing at 1,000°C. The microstructure was analyzed by SEM and the crystalline phases by X-ray diffraction (XRD). XRD showed that pre-sintered specimens contained tetragonal and monoclinic phases, while groups C and R showed tetragonal, cubic and monoclinic phases. After grinding, the cubic phase was eliminated in all groups. Annealing (DGR and WGR) resulted in only tetragonal phase. SEM showed semi-circular cracks after grinding and homogenization of particles after annealing. After grinding, surfaces show tetragonal and monoclinic phases and R can be assumed to be necessary prior to porcelain layering when grinding is performed.
All tested zirconia showed similar VHN, and the monolithic zirconia had similar roughness compared to one of the conventional zirconias. In addition, the monolithic zirconia showed similar flexural strength and Weibull modulus compared to the others even though its mean grain size was larger. The total transmittance of monolithic zirconia was higher than only one of the conventional zirconias tested.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.