The work function of indium tin oxide (ITO) substrates was modified with phosphonic acid molecular films. The ITO surfaces were treated prior to functionalization with a base cleaning procedure. The film growth and coverage were quantified by contact angle goniometry and XPS. Film orientation was determined by reflection/absorption infrared spectroscopy using ITO-on-Cr substrates. The absolute work functions of nitrophenyl- and cyanophenyl-phosphonic acid films in ITO were determined by Kelvin probe measurement to be 5.60 and 5.77 eV, respectively.

No abstract

No abstract

The addition of platinum metal to cobalt/alumina-based Fischer-Tropsch synthesis (FTS) catalysts increases both the reduction rate and, consequently, the density of active cobalt sites. Platinum also lowers the temperature of the two-step conversion of cobalt oxide to cobalt metal observed in temperature programmed reduction (TPR) as Co3O4 to CoO and CoO to Co0. The interaction of the alumina support with cobalt oxide ultimately determines the active site density of the catalyst surface. This interaction can be controlled by varying the cobalt loading and dispersion, selecting supports with differing surface areas or pore sizes, or changing the noble metal promoter. However, the active site density is observed to depend primarily on the cluster size and extent of reduction, and there is a direct relationship between site density and FTS rate. In this work, in situ extended X-ray absorption fine structure (EXAFS) at the LIII edge of Pt was used to show that isolated Pt atoms interact with supported cobalt clusters without forming observable Pt--Pt bonds. K-edge EXAFS was also used to verify that the cobalt cluster size increases slightly for those systems with Pt promotion. X-ray absorption near-edge spectroscopy (XANES) was used to examine the remaining cobalt clusters after the first stage of TPR, and it revealed that the species were almost entirely cobalt (II) oxide. After the second stage of TPR to form cobalt metal, a residual oxide persists in the sample, and this oxide has been identified as cobalt (II) aluminate using X-ray photoelectron spectroscopy (XPS). Sequential in situ reduction of promoted and unpromoted systems was also monitored through XPS, and Pt was seen to increase the extent of cobalt reduction by a factor of two.

No abstract

No abstract

Laser desorption mass spectroscopy has been used to characterize both modern and ∼ 150-year-old daguerreotypes. Such investigations are a necessary prelude to attempts to clean them of tarnish and other contaminants by laser ablation of the surface layers. Both positive- and negative-ion time-of-flight spectra were obtained following YAG laser ablation/desorption at 1064, 532, and 355 nm. Major peaks obtained from several daguerreotypes reveal expected elements from the substrate (Ag, Cu) as well as the developing (Hg) and gilding (Au) processes. Silver clusters (Agn) may reflect surface desorption of molecules or, alternatively, aggregates formed in the ejection process. Silver sulfide molecules observed from old daguerreotypes are the signature of the tarnishing process.

No abstract