We report on an investigation of quasi-free-standing graphene on 6H-SiC(0001)
which was prepared by intercalation of hydrogen under the buffer layer. Using
infrared absorption spectroscopy we prove that the SiC(0001) surface is
saturated with hydrogen. Raman spectra demonstrate the conversion of the buffer
layer into graphene which exhibits a slight tensile strain and short range
defects. The layers are hole doped (p = 5.0-6.5 x 10^12 cm^(-2)) with a carrier
mobility of 3,100 cm^2/Vs at room temperature. Compared to graphene on the
buffer layer a strongly reduced temperature dependence of the mobility is
observed for graphene on H-terminated SiC(0001)which justifies the term
"quasi-free-standing".Comment: 3 pages, 3 figures, accepted for publication in Applied Physics
Letter
We investigate the transport properties of high-quality single-layer graphene, epitaxially grown on a 6H-SiC͑0001͒ substrate. We have measured transport properties, in particular charge-carrier density, mobility, conductivity, and magnetoconductance of large samples as well as submicrometer-sized Hall bars which are entirely lying on atomically flat substrate terraces. The results display high mobilities, independent of sample size. The temperature dependence of the conductance indicates a rather strong coupling to the SiC substrate. An analysis of the Shubnikov-de Haas effect yields the Landau-level spectrum of single-layer graphene. When gated close to the Dirac point, the mobility increases substantially and the graphenelike quantum Hall effect occurs.
We investigate the magnetotransport in large area graphene Hall bars epitaxially grown on silicon carbide. In the intermediate field regime between weak localization and Landau quantization, the observed temperature-dependent parabolic magnetoresistivity is a manifestation of the electron-electron interaction. We can consistently describe the data with a model for diffusive (magneto)transport that also includes magnetic-field-dependent effects originating from ballistic time scales. We find an excellent agreement between the experimentally observed temperature dependence of magnetoresistivity and the theory of electron-electron interaction in the diffusive regime. We can further assign a temperature-driven crossover to the reduction of the multiplet modes contributing to electron-electron interaction from 7 to 3 due to intervalley scattering. In addition, we find a temperature-independent ballistic contribution to the magnetoresistivity in classically strong magnetic fields.
Graphene is an outstanding electronic material, predicted to have a role in post-silicon electronics. However, owing to the absence of an electronic bandgap, graphene switching devices with high on/off ratio are still lacking. Here in the search for a comprehensive concept for wafer-scale graphene electronics, we present a monolithic transistor that uses the entire material system epitaxial graphene on silicon carbide (0001). This system consists of the graphene layer with its vanishing energy gap, the underlying semiconductor and their common interface. The graphene/semiconductor interfaces are tailor-made for ohmic as well as for schottky contacts side-by-side on the same chip. We demonstrate normally on and normally off operation of a single transistor with on/off ratios exceeding 10 4 and no damping at megahertz frequencies. In its simplest realization, the fabrication process requires only one lithography step to build transistors, diodes, resistors and eventually integrated circuits without the need of metallic interconnects.
We report on a comprehensive study of the properties of quasi-freestanding monolayer and bilayer graphene produced by conversion of the (6√3×6√3)R30° reconstruction into graphene via intercalation of hydrogen. The conversion is confirmed by photoelectron spectroscopy and Raman spectroscopy. By using infrared absorption spectroscopy we show that the underlying SiC(0001) surface is terminated by hydrogen in the form of Si-H bonds. Using Hall effect measurements we have determined the carrier concentration and type as well as the mobility which lies well above 1000 cm2/Vs despite a significant amount of short range scatterers detected by Raman spectroscopy.
High-quality epitaxial graphene on silicon carbide (SiC) is today available in wafer size. Similar to exfoliated graphene, its charge carriers are governed by the Dirac-Weyl Hamiltonian and it shows excellent mobilities. For many experiments with graphene, in particular for surface science, a bottom gate is desirable. Commonly, exfoliated graphene flakes are placed on an oxidized silicon wafer that readily provides a bottom gate. However, this cannot be applied to epitaxial graphene as the SiC provides the source material out of which graphene grows. Here, we present a reliable scheme for the fabrication of bottom-gated epitaxial graphene devices, which is based on nitrogen (N) implantation into a SiC wafer and subsequent graphene growth. We demonstrate working devices in a broad temperature range from 6 to 300 K. Two gating regimes can be addressed, which opens a wide engineering space for tailored devices by controlling the doping of the gate structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.