An AC-DC combined voltage is applied to the oil-pressboard insulation near the valve side during the operation of a converter transformer. To study the breakdown characteristics of an oil-pressboard insulation under such voltages, a typical plate electrode structure was employed in the laboratory to conduct a breakdown test on the oil-pressboard insulation. The electrical field distribution and the DC contents of the transformer oil and the pressboard in composite insulation under the AC-DC combined voltage were simulated by their dielectric parameters. The breakdown strength of the transformer oil decreases with the increase in the DC content of the applied voltage, whereas that of the pressboard increases. For the oil-pressboard insulation, the breakdown voltage increases first and then decreases. The electric field strength decreases in the transformer oil with the increase in the DC content, whereas it increases in the pressboard. And the DC contents of the transformer and the pressboard in composite insulation were different from that of the applied voltage. Finally, based on the above results, a mathematical model was proposed to describe the breakdown characteristics of the oil-pressboard insulation under the AC-DC combined voltage; the theoretical and experimental results were in good agreement.
High-voltage direct-current (HVDC) dry bushing capacitor-core insulation is composed of epoxy resin-impregnated insulating paper (RIP). To improve the thermal conductivity, breakdown strength, and space charge characteristics of RIP, 0.1 wt % nano-cellulose fiber (CNF)-modified RIP (CNF/RIP), 2.5–30 wt % hexagonal boron nitride (h-BN)-modified RIP (h-BN/RIP), and 2.5–30 wt % h-BN + 0.1 wt % CNF-modified RIP (h-BN + 0.1 wt % CNF/RIP) were prepared. Scanning electron microscopy (SEM) was implemented; the thermal conductivity, DC conductivity, DC breakdown strength, and space charge characteristics were tested. The maximum thermal conductivity of h-BN + 0.1 wt % CNF/RIP was 0.376 W/m.K with a h-BN content of 30 wt %. The thermal conductivity was 85.2% higher than that of unmodified RIP. The breakdown strength and charge suppression were the best in the case of 10 wt % h-BN + 0.1 wt % CNF/RIP. The maximum breakdown strength was 11.2% higher than that of unmodified RIP. These results can play a significant role in the research and development of insulation materials for HVDC dry bushing.
The space charge accumulation is an important factor to design the oil-pressboard composite insulation of convertor transformer, which is greatly affected by the temperature. In this paper, the space charge accumulation and attenuation in the two layers and single layer under DC voltage were studied by the Pulsed Electro-Acoustic Method from 20 • C to 60 • C, and the electric field distribution was calculated by the space charge distribution. The studied results have indicated that the distributions of space charge and electric field in the test results do not follow the Maxwell-Wagner polarization. The space charge distribution is affected by the surface trap, bulk trap, charge migration and electric field. The temperature affected the polarity and amount of the charge at oil-pressboard interface. The space charge accumulation of the two layers is more complex than that of the single layer, and the space charge accumulation and attenuation of two layers need longer time to reach the stable stage. The space charge accumulation in the single layer is largest at 40 • C, whereas the space charge accumulation in the two layers is largest at 20 • C. Moreover, the increase in the temperature increases the attenuation amplitude and speed of space charge. INDEX TERMS Space charge, two layers, oil-pressboard insulation, temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.