Purpose -The purpose of this paper is to report a study about the rapid prototyping method of dental glass-ceramic restoration. Design/methodology/approach -Dental glass-ceramic restoration materials have excellent physical and chemical, mechanical, aesthetic and biocompatibility characteristics. However, casting methods adopted at present have complicated procedures and high costs; the forming qualities are especially difficult to control. These problems greatly restrict their clinical application and promotion. Therefore, a new forming process based on selective laser sintering (SLS) technology is proposed. First, dental glass-ceramic is processed into fine powder through a special heat treatment process. Then, the dental restoration parts are manufactured using SLS without any moulds. In this paper, the effects of processing parameters including laser power, scan speed, scan spacing and preheating temperature on the relative density and mechanical properties of the sintered parts are studied. Findings -The experimental results have shown that for the composite powder of epoxy resin binder E-12 and K 2 O-Al 2 O 3 -SiO 2 series of dental glassceramics, when preheating temperature, layer thickness, laser power, scan speed and scan spacing are, respectively, 30 , 358C, 0.08 mm, 21 W, 1,800 mm/s and 0.10 mm/s, the relative densities of dental glass-ceramic parts are relatively high; the mechanical properties and forming effect are excellent. The relative density and bending strength of SLS parts under the optimized processing parameters are 37.40 per cent and 2.08 MPa, respectively.Research limitations/implications -This study only concerns the preparation and SLS of the dental glass-ceramic powders. Further investigations are planned to be conducted on post processing, such as binder decomposition, isostatic press and high temperature sintering. Originality/value -This study will provide a theoretical and technical basis for dental glass-ceramic restorations of SLS.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.