Poly(lactic-co-glycolic acid) (PLGA) tubes (5 mm in diameter) were fabricated using an electro spinning method and used as a scaffold for artificial blood vessels through the hybridization of smooth muscle cells (SMCs) and endothelial cells (ECs) differentiated from canine bone marrow under previously reported conditions. The potential clinical applications of these artificial blood vessels were investigated using a canine model. From the results, the tubular-type PLGA scaffolds for artificial blood vessels showed good mechanical strength, and the duallayered blood vessels showed acceptable hybridization behavior with ECs and SMCs. The artificial blood vessels were implanted and substituted for an artery in an adult dog over a 3-week period. The hybridized blood vessels showed neointimal formation with good patency. However, the control vessel (unhybridized vessel) was occluded during the early stages of implantation. These results suggest a shortcut for the development of small diameter, tubular-type, nanofiber blood vessels using a biodegradable material (PLGA).
The surfaces of Nitinol (TiNi), a popular metal alloy for arterial stents were thin-coated with diamond-like carbon (DLC) and then grafted with poly(ethylene glycol) (PEG) to increase biocompatibility. The TiNi control, DLC-coated TiNi (TiNi—DLC), and the PEG-grafted TiNi—DLC (TiNi—DLC—PEG) surface characteristics and biocompatibility were evaluated. The hydrophilicity of the TiNi—DLC—PEG significantly increased and the amount of both oxygen and nitrogen on the TiNi—DLC—PEG also increased compared to the TiNi control and TiNi—DLC due to the grafted PEG. The ratio between albumin and fibrinogen was higher on the PEG-grafted surface than the other surfaces when tested with human blood components; the platelet adhesion decreased the most on the TiNi—DLC—PEG surface, indicating improved blood compatibility. For in vivo tests using a rat model, the samples that were implanted for 6 weeks formed fibrous tissue; the tissue layer was much thinner on the PEG-grafted sample than the other two groups. The present results indicate that PEG-grafted TiNi—DLC surface may be effective in enhancing biocompatibility of blood-contacting biomaterials including vascular stents.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.