Abstract:Dextran-based hydrogels were obtained by polymerization of aqueous solutions of methacrylated dextran (dex-MA) or lactate-hydroxyethyl methacrylate-derivatized dextran (dex-lactate-HEMA). Both nondegradable dex-MA and degradable dex-lactate-HEMA disk-shaped hydrogels, varying in initial water content and degree of substitution (DS, the number of methacrylate groups per 100 glucose units), were implanted subcutaneously in rats. The tissue reaction was evaluated over a period of 6 weeks. The initial foreign-body reaction to the dex-MA hydrogels was characterized by infiltration of granulocytes and macrophages and the formation of fibrin, and exudate, as well as new blood vessels. This reaction depended on the initial water content as well as on the DS of the hydrogel and decreased within 10 days. The mildest tissue response was observed for the gel with the highest water content and intermediate DS. At day 21 all dex-MA hydrogels were surrounded by a fibrous capsule and no toxic effects on the surrounding tissue were found. No signs of degradation were observed. The initial foreign-body reaction to the degradable dex-lactate-HEMA hydrogels was less severe compared with the dex-MA gels. In general, the size of the dex-lactate-HEMA hydrogels increased progressively with time and finally the gels completely dissolved. Degradation of the dex-lactate-HEMA hydrogels was associated with infiltration of macrophages and the formation of giant cells, both of which phagocytosed pieces of the hydrogel. A good correlation between the in vitro and the in vivo degradation time was found. This suggests that extra-cellular degradation is not caused by enzymes but depends only on hydrolysis of the ester and/or carbonate bonds present in the crosslinks of the hydrogels. After 21 days, the degradable hydrogels, as such, could not be retrieved, but accumulation of macrophages and giant cells was observed, both of which contained particles of the gels intracellularly. As for the dex-MA hydrogels, no toxic effects on the surrounding tissue were found. The results presented in this study demonstrate that dextran-based hydrogels can be considered as biocompatible materials, making these hydrogels attractive systems for drug delivery purposes.
Microspheres based on methacrylated dextran (dex-MA), dextran derivatized with lactate-hydroxyethyl methacrylate (dex-lactate-HEMA) or derivatized with HEMA (dex-HEMA) were prepared. The microspheres were injected subcutaneously in rats and the effect of the particle size and network characteristics [initial water content and degree of methacrylate substitution (DS)] on the tissue reaction was investigated for 6 weeks. As a control, poly(lactic-co-glycolic)acid (PLGA) microspheres with varying sizes (unsized, smaller than 10 microm, smaller and larger than 20 microm) were injected as well. A mild tissue reaction to the PLGA microspheres was observed, characterized by infiltration of macrophages (MØs) and some granulocytes. Six weeks postinjection, the PLGA microspheres were still present. However, their size was decreased indicating degradation and many spheres had been phagocytosed. The tissue reaction was hardly affected by size differences, except for particles smaller than 10 microm, which induced an extensive tissue reaction. The initial tissue reaction to nondegradable dex-MA microspheres was stronger than towards the PLGA microspheres, but at day 10 the tissue reactions were comparable for both groups. Six weeks postinjection, the dex-MA microspheres were completely phagocytosed, and no signs of degradation were observed. The size and initial water content of dex-MA microspheres hardly affected the tissue response, although less granulocytes were observed for microspheres with higher DS. Slowly degrading dextran microspheres composed of dex-(lactate(1)-)HEMA induced a tissue reaction comparable to the PLGA microspheres. However, degradation of the dex-(lactate(1,3)-)HEMA microspheres was associated with an increased number of MØ's and giant cells, both phagocytosing the microspheres and their degradation products. Similar to PLGA, no adverse reactions were observed for the nondegradable dex-MA and degradable dextran microspheres. This study shows that both nondegradable and degradable dextran-based microspheres are well tolerated after subcutaneous injection in rats, which make them interesting candidates as controlled drug delivery systems.
Dextran-based hydrogels were obtained by polymerization of aqueous solutions of methacrylated dextran (dex-MA) or lactate-hydroxyethyl methacrylate-derivatized dextran (dex-lactate-HEMA). Both nondegradable dex-MA and degradable dex-lactate-HEMA disk-shaped hydrogels, varying in initial water content and degree of substitution (DS, the number of methacrylate groups per 100 glucose units), were implanted subcutaneously in rats. The tissue reaction was evaluated over a period of 6 weeks. The initial foreign-body reaction to the dex-MA hydrogels was characterized by infiltration of granulocytes and macrophages and the formation of fibrin, and exudate, as well as new blood vessels. This reaction depended on the initial water content as well as on the DS of the hydrogel and decreased within 10 days. The mildest tissue response was observed for the gel with the highest water content and intermediate DS. At day 21 all dex-MA hydrogels were surrounded by a fibrous capsule and no toxic effects on the surrounding tissue were found. No signs of degradation were observed. The initial foreign-body reaction to the degradable dex-lactate-HEMA hydrogels was less severe compared with the dex-MA gels. In general, the size of the dex-lactate-HEMA hydrogels increased progressively with time and finally the gels completely dissolved. Degradation of the dex-lactate-HEMA hydrogels was associated with infiltration of macrophages and the formation of giant cells, both of which phagocytosed pieces of the hydrogel. A good correlation between the in vitro and the in vivo degradation time was found. This suggests that extra-cellular degradation is not caused by enzymes but depends only on hydrolysis of the ester and/or carbonate bonds present in the crosslinks of the hydrogels. After 21 days, the degradable hydrogels, as such, could not be retrieved, but accumulation of macrophages and giant cells was observed, both of which contained particles of the gels intracellularly. As for the dex-MA hydrogels, no toxic effects on the surrounding tissue were found. The results presented in this study demonstrate that dextran-based hydrogels can be considered as biocompatible materials, making these hydrogels attractive systems for drug delivery purposes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.