3D printing has the potential to deliver personalized implants and devices for obstetric and gynecologic applications. The aim of this study is to engineer customizable and biodegradable 3D printed implant materials that can elute estrogen and/or progesterone. All 3D constructs were printed using polycaprolactone (PCL) biodegradable polymer laden with estrogen or progesterone and were subjected to hormone-release profile studies using ELISA kits. Material thermal properties were tested using thermogravimetric analysis and differential scanning calorimetry. The 3D printed constructs showed extended hormonal release over a one week period. Cytocompatibility and bioactivity were assessed using a luciferase assay. The hormone-laden 3D printed constructs demonstrated an increase in luciferase activity and without any deleterious effects. Thermal properties of the PCL and hormones showed degradation temperatures above that of the temperature used in the additive manufacturing process–suggesting that 3D printing can be achieved below the degradation temperatures of the hormones. Sample constructs in the shape of surgical meshes, subdermal rods, intrauterine devices and pessaries were designed and printed. 3D printing of estrogen and progesterone-eluting constructs was feasible in this proof of concept study. These custom designs have the potential to act as a form of personalized medicine for drug delivery and optimized fit based on patient-specific anatomy.
The 3D printing manufacturing method to create instruments in percutaneous procedures is feasible. Further in vivo studies will substantiate these findings.
Additive manufacturing has great potential for personalized medicine in osseous fixation surgery, including maxillofacial and orthopedic applications. The purpose of this study was to demonstrate 3D printing methods for the fabrication of patient-specific fixation implants that allow for localized drug delivery. 3D printing was used to fabricate gentamicin (GS) and methotrexate (MTX)-loaded fixation devices, including screws, pins, and bone plates. Scaffolds with different infill ratios of polylactic acid (PLA), both without drugs and impregnated with GS and MTX, were printed into cylindrical and rectangular-shaped constructs for compressive and flexural strength mechanical testing, respectively. Bland PLA constructs showed significantly higher flexural strength when printed in a Y axis at 100% infill compared to other axes and infill ratios; however, there was no significant difference in flexural strength between other axes and infill ratios. GS and MTX-impregnated constructs had significantly lower flexural and compressive strength as compared to the bland PLA constructs. GS-impregnated implants demonstrated bacterial inhibition in plate cultures. Similarly, MTX-impregnated implants demonstrated a cytotoxic effect in osteosarcoma assays. This proof of concept work shows the potential of developing 3D printed screws and plating materials with the requisite mechanical properties and orientations. Drug-impregnated implants were technically successful and had an anti-bacterial and chemotherapeutic effect, but drug addition significantly decreased the flexural and compressive strengths of the custom implants.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.